PPO NORYL™ NH6020-100 SABIC INNOVATIVE NETHERLANDS
129
- Unit Price:
- $3753 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan High mobility Glass fiber reinforced
- Application Areas:Electrical applications Automotive interior parts
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | 饱和,23°C | ISO62 | 0.18 | % |
| 平衡,23°C,50%RH | ISO62 | 0.060 | % | |
| density | ASTMD792,ISO1183 | 1.14 | g/cm³ | |
| Melt mass flow rate | 280°C/5.0kg | ASTMD1238 | 14 | g/10min |
| Melt volume flow rate | 280°C/5.0kg | ISO1133 | 11.6 | cm3/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50到0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| elongation | 屈服 | ISO527-2/50 | 4.6 | % |
| 断裂4 | ASTMD638 | 6.1 | % | |
| 断裂 | ISO527-2/50 | 4.2 | % | |
| Bending modulus | 50.0mm跨距5 | ASTMD790 | 3020 | Mpa |
| --6 | ISO178 | 2690 | Mpa | |
| Bending stress | --6,7 | ISO178 | 114 | Mpa |
| 屈服,50.0mm跨距5 | ASTMD790 | 121 | Mpa | |
| Tensile modulus | --3 | ASTMD638 | 2740 | Mpa |
| -- | ISO527-2/1 | 2740 | Mpa | |
| Tensile strength | 屈服4 | ASTMD638 | 78.9 | Mpa |
| 屈服 | ISO527-2/50 | 77.4 | Mpa | |
| 断裂4 | ASTMD638 | 67.6 | Mpa | |
| 断裂 | ISO527-2/50 | 56.6 | Mpa | |
| elongation | 屈服4 | ASTMD638 | 4.6 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 7.8E-05 | cm/cm/°C |
| MD:-40到40°C | ISO11359-2 | 7.5E-05 | cm/cm/°C | |
| TD:-40到40°C | ASTME831 | 7E-06 | cm/cm/°C | |
| TD:-40到40°C | ISO11359-2 | 7.8E-05 | cm/cm/°C | |
| RTIElec | UL746 | 110 | °C | |
| Evolution Calendar intelligent importer | UL746 | 105 | °C | |
| Vicat softening temperature | -- | ISO306/B50 | 141 | °C |
| -- | ISO306/B120 | 151 | °C | |
| Hot deformation temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 125 | °C |
| 1.8MPa,未退火,64.0mm跨距10 | ISO75-2/Af | 125 | °C | |
| Vicat softening temperature | -- | ASTMD152511 | 150 | °C |
| RTI | UL746 | 110 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | IEC60093 | 2.5E+16到4.2E+16 | ohms·cm | |
| Dielectric strength | 1.60mm,在油中 | IEC60243-1 | 27 | KV/mm |
| Leakage Trace Index | IEC60112 | 600 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTMD256 | 49 | J/m |
| -30°C9 | ISO180/1A | 5.4 | kJ/m² | |
| 23°C9 | ISO180/1A | 8.1 | kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 18.4 | J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 9.8 | kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ASTMD256 | 36 | J/m |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning wire flammability index | 1.0mm | IEC60695-2-12 | 960 | °C |
| Hot filament ignition temperature | 1.0mm | IEC60695-2-13 | 825 | °C |
| 2.0mm | IEC60695-2-13 | 800 | °C | |
| 3.0mm | IEC60695-2-13 | 800 | °C | |
| Extreme Oxygen Index | ISO4589-2 | 37 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.