PPO NORYL GTX™ PPX830 SABIC INNOVATIVE SHANGHAI
1102
- Unit Price:
- $4000 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Dimensional stability High impact High rigidity
- Application Areas:Printer components Cold water pipe applicati Water heater
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.20to0.25 | % |
| TD：3.20mm | 内部方法 | 0.40to0.60 | % | |
| Melt mass flow rate | 280°C/5.0kg | ASTMD1238 | 6.0 | g/10min |
| Melt volume flow rate | 280°C/5.0kg | ISO1133 | 6.00 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending strength 5,6 | ISO178 | 141 | Mpa | |
| Tensile modulus | ISO527-2/1 | 7700 | Mpa | |
| Elongation rate 4 | Break | ASTMD638 | 100 | % |
| Bending modulus 5 | ISO178 | 7100 | Mpa | |
| Tensile stress | Yield | ISO527-2/5 | 98.0 | Mpa |
| Break | ISO527-2/5 | 98.0 | Mpa | |
| Tensile strain | Yield | ISO527-2/5 | 3.2 | % |
| Break | ISO527-2/5 | 3.2 | % | |
| Elongation rate 3 | Yield | ASTMD638 | 2.9 | % |
| Tensile modulus 2 | ASTMD638 | 7600 | Mpa | |
| Tensile strength 3 | Break | ASTMD638 | 101 | Mpa |
| Yield | ASTMD638 | 101 | Mpa | |
| Bending modulus 4 | 50.0mmSpan | ASTMD790 | 6600 | Mpa |
| Bending strength 4 | Yield,50.0mmSpan | ASTMD790 | 144 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | TD：-30to80°C | ISO11359-2 | 1.2E-04 | cm/cm/°C |
| MD：-40to95°C | ASTME831 | 2.5E-05 | cm/cm/°C | |
| MD：-30to80°C | ISO11359-2 | 2.5E-05 | cm/cm/°C | |
| TD：-40to95°C | ASTME831 | 1.3E-04 | cm/cm/°C | |
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 166 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 156 | °C | |
| Vicat softening temperature | ISO306/B120 | 150 | °C | |
| BallPressure Test | 125°C | IEC60695-10-2 | Pass | |
| Hot deformation temperature 9 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 153 | °C |
| 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 168 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| The impact strength of a simply supported beam without a notch is 7 | -30°C | ISO179/1eU | 36 | kJ/m² |
| 23°C | ISO179/1eU | 39 | kJ/m² | |
| NotchedIzodImpactStrength8 | 23°C | ISO180/1A | 10 | kJ/m² |
| Unscented Izod Impact Strength 8 | -30°C | ISO180/1U | 42 | kJ/m² |
| 23°C | ISO180/1U | 42 | kJ/m² | |
| Dart impact equipped with measuring instruments | -30°C,TotalEnergy | ASTMD3763 | 10.0 | J |
| 23°C,TotalEnergy | ASTMD3763 | 15.0 | J |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | 1.0mm | UL94 | HB | |
| Burning wire flammability index | 3.0mm | IEC60695-2-12 | 650 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.