PPO NORYL GTX™ GTX810-51511OD SABIC INNOVATIVE US
139
Unit Price:$4959 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Chemical resistance enhance High temperature resistan
- Application Areas:Casters fibre
- Color:--
- Grade:--
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 收缩率 | 流动 : 3.20 mm | 内部方法 | 0.60 到 0.80 | % |
| 横向流动 : 3.20 mm | 内部方法 | 0.65 到 0.85 | % | |
| 吸水率 | 24 hr, 50% RH | ASTM D570 | 0.50 | % |
| 平衡, 50% RH | ASTM D570 | 1.0 | % |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 伸长率 | 断裂 | ASTM D638 | 10 | % |
| 洛氏硬度 | R 级 | ASTM D785 | 119 | |
| 弯曲模量 | 100 mm 跨距 | ASTM D790 | 3960 | Mpa |
| 弯曲强度 | 屈服, 100 mm 跨距 | ASTM D790 | 155 | Mpa |
| 抗张强度 | 屈服 | ASTM D638 | 89.0 | Mpa |
| 断裂 | ASTM D638 | 88.0 | Mpa |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 维卡软化温度 | ASTM D15253 | 240 | °C | |
| 线形热膨胀系数 - 流动 | -20 到 150°C | ASTM E831 | 4.0E-5 到 5.0E-5 | cm/cm/°C |
| RTI | UL 746 | 50.0 | °C | |
| RTI Imp | UL 746 | 50.0 | °C | |
| RTI Elec | UL 746 | 50.0 | °C | |
| 载荷下热变形温度 | 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 245 | °C |
| 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 210 | °C |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 相比耐漏电起痕指数(CTI) | UL 746 | PLC 3 | ||
| 热丝引燃 (HWI) | UL 746 | PLC 0 | ||
| 高电弧燃烧指数(HAI) | UL 746 | PLC 0 | ||
| 高电压电弧起痕速率 (HVTR) | UL 746 | PLC 3 | ||
| 耐电弧性 | ASTM D495 | PLC 6 |
| 注射 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 干燥时间 | 3.0 到 4.0 | hr | ||
| 建议注射量 | 30 到 50 | % | ||
| 料筒后部温度 | 265 到 305 | °C | ||
| 料筒中部温度 | 270 到 305 | °C | ||
| 料筒前部温度 | 275 到 305 | °C | ||
| 射嘴温度 | 280 到 305 | °C | ||
| 背压 | 0.300 到 1.40 | Mpa | ||
| 螺杆转速 | 20 到 100 | rpm | ||
| 排气孔深度 | 0.013 到 0.038 | mm | ||
| 干燥温度 | 95 到 105 | °C | ||
| 建议的最大水分含量 | 0.070 | % | ||
| 加工（熔体）温度 | 280 到 305 | °C | ||
| 模具温度 | 75 到 120 | °C |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL 阻燃等级 | 1.5 mm | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.