PPO NORYL™ SE10000 SABIC INNOVATIVE SHANGHAI
120
- Unit Price:
- $3506 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan Hydrolysis resistance
- Application Areas:Household appliances Automotive components
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| TD2 | 内部方法 | 0.50to0.70 | % | |
| Water absorption rate | 24hr | ASTMD570 | 0.060 | % |
| Melt mass flow rate | 280°C/5.0kg | ASTMD1238 | 8.5 | g/10min |
| Melt volume flow rate | 280°C/5.0kg | ISO1133 | 8.70 | cm3/10min |
| Outdoor applicability | UL746C | f1 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus 3 | ASTMD638 | 2500 | Mpa | |
| Tensile strength 4 | Break | ASTMD638 | 53.1 | Mpa |
| Bending modulus 7 | ISO178 | 2560 | Mpa | |
| Bending strength 7,8 | ISO178 | 99.5 | Mpa | |
| Tensile stress | Break | ISO527-2/50 | 50.8 | Mpa |
| Yield | ISO527-2/50 | 61.3 | Mpa | |
| Tensile strain | Yield | ISO527-2/50 | 4.3 | % |
| Break | ISO527-2/50 | 21 | % | |
| Tensile modulus | ISO527-2/1 | 2670 | Mpa | |
| Bending modulus | 100mmSpan6 | ASTMD790 | 2400 | Mpa |
| 50.0mmSpan5 | ASTMD790 | 2700 | Mpa | |
| bending strength | Yield,50.0mmSpan5 | ASTMD790 | 100 | Mpa |
| Yield,100mmSpan6 | ASTMD790 | 98.0 | Mpa | |
| Elongation rate 4 | Break | ASTMD638 | 15 | % |
| Yield | ASTMD638 | 4.0 | % | |
| Tensile strength 4 | Yield | ASTMD638 | 65.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 127 | °C |
| 0.45MPa,Unannealed,6.40mm | ASTMD648 | 129 | °C | |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 118 | °C | |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 113 | °C | |
| RTIElec | UL746 | 110 | °C | |
| Evolution Calendar intelligent importer | UL746 | 105 | °C | |
| RTIStr | UL746 | 110 | °C | |
| Hot deformation temperature 10 | 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 115 | °C |
| 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 129 | °C | |
| Vicat softening temperature | -- | ISO306/B120 | 135 | °C |
| -- | ISO306/B50 | 132 | °C | |
| Linear coefficient of thermal expansion | TD：-40to40°C | ASTME831 | 8.8E-05 | cm/cm/°C |
| MD：-40to40°C | ASTME831 | 8E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | 3.20mm,inOil | ASTMD149 | 18 | KV/mm |
| Compared to the anti leakage trace index | CTI | UL746 | PLC1 | |
| Arc resistance 11 | ASTMD495 | PLC6 | ||
| Dissipation factor | 50Hz | ASTMD150 | 3.4E-03 | |
| 60Hz | ASTMD150 | 3.4E-03 | ||
| 1MHz | ASTMD150 | 2.1E-03 | ||
| Surface resistivity | ASTMD257 | >1.0E+15 | ohms | |
| Dielectric constant | 50Hz | ASTMD150 | 2.52 | |
| 60Hz | ASTMD150 | 2.52 | ||
| 1MHz | ASTMD150 | 2.46 | ||
| Volume resistivity | ASTMD257 | 2.3E+16 | ohms·cm | |
| High voltage arc tracing rate | HVTR | UL746 | PLC4 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| NotchedIzodImpactStrength9 | 23°C | ISO180/1A | 15 | kJ/m² |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 49.7 | J |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | V-1 | |
| 6.0mm | UL94 | V-0 | ||
| RadiantPanelListing(UL) | UL94 | RP100 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.