PPO NORYL™ SE1GFN2 WH50030 SABIC INNOVATIVE US
162
- Unit Price:US$ 4,771 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:35MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:enhance｜Glass fiber reinforced
- Application Areas:Electronic communication accessories｜Electronic communication accessories
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 3.5 g/10 min | |
| Melt volume flow rate | ISO 1133 | 3.00 cm3/10min | |
| Shrinkage rate | 内部方法 | 0.20 - 0.50 % | |
| Water absorption rate | ISO 62 | 0.11 % | |
| ISO 62 | 0.040 % |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 玻纤增强 | ||
| Color | 本白色 | ||
| purpose | 车辆配件 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-1 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 7100 Mpa | |
| ISO 527-2/1 | 6400 Mpa | ||
| tensile strength | ASTM D638 | 120 Mpa | |
| ISO 527-2/50 | 100 Mpa | ||
| elongation | ASTM D638 | 3.0 % | |
| ISO 527-2/50 | 2.5 % | ||
| Flexural modulus | ASTM D790 | 5500 Mpa | |
| ISO 178 | 5600 Mpa | ||
| bending strength | ISO 178 | 150 Mpa | |
| ASTM D790 | 140 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ASTM D4812 | 520 J/m | |
| ISO 180/1U | 27 kJ/m² | ||
| ISO 180/1U | 28 kJ/m² | ||
| Dart impact | ASTM D3763 | 18.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 1.3E+17 ohms | |
| Volume resistivity | ASTM D257 | 2.0E+16 ohms·cm | |
| dielectric strength | ASTM D149 | 26 KV/mm | |
| IEC 60243-1 | 26 KV/mm | ||
| dielectric constant | ASTM D150 | 2.93 | |
| IEC 60250 | 2.90 | ||
| Dissipation Factor | ASTM D150 | 3.4E-3 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 110 to 120 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 30 to 70 % | ||
| Temperature at the rear of the barrel | 265 to 315 °C | ||
| Temperature in the middle of the barrel | 275 to 320 °C | ||
| Temperature at the front of the material cylinder | 290 to 325 °C | ||
| Spray nozzle temperature | 300 to 325 °C | ||
| Processing (melt) temperature | 300 to 325 °C | ||
| Temperature | 80 to 110 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| screw speed | 20 to 100 rpm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 142 °C | |
| ASTM D648 | 134 °C | ||
| ISO 75-2/Af | 133 °C | ||
| vicat | ASTM D15259 | 142 °C | |
| ISO 306/B120 | 144 °C | ||
| Linear coefficient of thermal expansion | ASTM E831 | 2.5E-5 cm/cm/°C | |
| ISO 11359-2 | 3.0E-5 cm/cm/°C | ||
| ASTM E831 | 7.5E-5 cm/cm/°C | ||
| ISO 11359-2 | 7.5E-5 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.