PPO NORYL™ GFN1-111 SABIC INNOVATIVE SHANGHAI
126
- Unit Price:
- $4123 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan Hydrolysis resistance
- Application Areas:Connector Automotive components
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 300°C/5.0kg | ASTMD1238 | 17 | g/10min |
| Melt volume flow rate | 300°C/5.0kg | ISO1133 | 16.4 | cm3/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.20to0.50 | % |
| Water absorption rate | 24hr | ASTMD570 | 0.060 | % |
| Outdoor applicability | UL746C | f1 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus 2 | ASTMD638 | 4350 | Mpa | |
| Tensile modulus | ISO527-2/1 | 4400 | Mpa | |
| Tensile strength 3 | Break | ASTMD638 | 63.0 | Mpa |
| Tensile stress | Break | ISO527-2 | 64.0 | Mpa |
| elongation | Break | ASTMD638 | 3.0 | % |
| Tensile strain | Break | ISO527-2 | 3.0 | % |
| Bending modulus | 50.0mmSpan4 | ASTMD790 | 3840 | Mpa |
| 100mmSpan5 | ASTMD790 | 3590 | Mpa | |
| ISO178 | 4160 | Mpa | ||
| Bending stress | ISO178 | 122 | Mpa | |
| bending strength | Yield,50.0mmSpan4 | ASTMD790 | 116 | Mpa |
| Yield,100mmSpan5 | ASTMD790 | 108 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| RTIElec | UL746 | 90.0 | °C | |
| Evolution Calendar intelligent importer | UL746 | 90.0 | °C | |
| RTIStr | UL746 | 90.0 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 131 | °C |
| Hot deformation temperature 8 | 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 132 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 122 | °C |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 125 | °C | |
| Hot deformation temperature 8 | 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 124 | °C |
| Vicat softening temperature | -- | ISO306/B50 | 131 | °C |
| -- | ISO306/B120 | 134 | °C | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 5.1E-05 | cm/cm/°C |
| TD：-40to40°C | ASTME831 | 7.1E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric constant | 1MHz | ASTMD150 | 2.90 | |
| Dissipation factor | 1MHz | ASTMD150 | 1.4E-03 | |
| Arc resistance 9 | ASTMD495 | PLC7 | ||
| High arc combustion index | HAI | UL746 | PLC4 | |
| High voltage arc tracing rate | HVTR | UL746 | PLC4 | |
| Hot wire ignition | HWI | UL746 | PLC5 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Simple supported beam without notch impact strength 6 | -30°C | ISO179/1eU | 33 | kJ/m² |
| 23°C | ISO179/1eU | 35 | kJ/m² | |
| Suspended wall beam gap impact strength 7 | -30°C | ISO180/1A | 9.4 | kJ/m² |
| 23°C | ISO180/1A | 11 | kJ/m² | |
| Unscented Izod Impact Strength 7 | -30°C | ISO180/1U | 25 | kJ/m² |
| 23°C | ISO180/1U | 28 | kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 21.7 | J |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | L-Sale | ASTMD785 | 104 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.