PPO NORYL™ ENG265-8746S NR4N77 SABIC INNOVATIVE US
115
- Unit Price:
- $3753 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability Glass fiber reinforced
- Application Areas:Pipe fittings Profile medical care
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| Water absorption rate | 24hr | ASTMD570 | 0.060 | % |
| Melt mass flow rate | 280°C/5.0kg | ASTMD1238 | 8.5 | g/10min |
| Melt volume flow rate | 280°C/5.0kg | ISO1133 | 8.70 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength | Break | ASTMD638 | 50.0 | Mpa |
| Bending stress | ISO178 | 95.0 | Mpa | |
| Tensile modulus 2 | ASTMD638 | 2400 | Mpa | |
| Tensile strength 3 | Yield | ASTMD638 | 56.0 | Mpa |
| Elongation rate 4 | Break | ASTMD638 | 28 | % |
| Tensile stress | Break | ISO527-2 | 50.0 | Mpa |
| Yield | ISO527-2 | 55.0 | Mpa | |
| Tensile strain | Break | ISO527-2 | 27 | % |
| Yield | ISO527-2 | 3.1 | % | |
| Tensile modulus | ISO527-2/1 | 2550 | Mpa | |
| elongation | Yield | ASTMD638 | 3.3 | % |
| Bending modulus | 50.0mmSpan4 | ASTMD790 | 2550 | Mpa |
| 100mmSpan5 | ASTMD790 | 2450 | Mpa | |
| ISO178 | 2500 | Mpa | ||
| bending strength | Yield,50.0mmSpan4 | ASTMD790 | 89.0 | Mpa |
| Yield,100mmSpan5 | ASTMD790 | 88.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 132 | °C |
| 0.45MPa,Unannealed,6.40mm | ASTMD648 | 137 | °C | |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 118 | °C | |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 126 | °C | |
| RTIElec | UL746 | 105 | °C | |
| Evolution Calendar intelligent importer | UL746 | 90.0 | °C | |
| RTIStr | UL746 | 105 | °C | |
| Vicat softening temperature | -- | ISO306/B50 | 137 | °C |
| -- | ISO306/B120 | 141 | °C | |
| Linear coefficient of thermal expansion | MD：-40to95°C | ASTME831 | 5.9E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | 3.20mm,inOil | ASTMD149 | 20 | KV/mm |
| Compared to the anti leakage trace index | CTI | UL746 | PLC3 | |
| Arc resistance 7 | ASTMD495 | PLC7 | ||
| Hot wire ignition | HWI | UL746 | PLC2 | |
| High arc combustion index | HAI | UL746 | PLC0 | |
| High voltage arc tracing rate | HVTR | UL746 | PLC4 | |
| Dissipation factor | 50Hz | ASTMD150 | 4E-04 | |
| 60Hz | ASTMD150 | 4E-04 | ||
| Dielectric constant | 50Hz | ASTMD150 | 2.65 | |
| 60Hz | ASTMD150 | 2.65 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Suspended wall beam notch impact strength 6 | -30°C | ISO180/1A | 8.7 | kJ/m² |
| 23°C | ISO180/1A | 13 | kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 39.0 | J |
| Falling hammer impact | -40°C | ASTMD3029 | 5.42 | J |
| -30°C | ASTMD3029 | 25.8 | J |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ASTMD785 | 119 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.