PPO NORYL™ V0150B-701 SABIC INNOVATIVE US
124
- Unit Price:
- $4432 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability Glass fiber reinforced
- Application Areas:medical care
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：--2 | 内部方法 | 0.50to0.70 | % |
| MD：3.20mm | 内部方法 | 0.50to0.70 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.18 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.060 | % | |
| Melt mass flow rate | 280°C/5.0kg | ASTMD1238 | 3.5 | g/10min |
| Melt volume flow rate | 300°C/5.0kg | ISO1133 | 10.0 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Taber abraser | 1000Cycles,1000g,CS-17Wheel | 内部方法 | 35.0 | mg |
| Tensile stress | Yield | ISO527-2/50 | 70.0 | Mpa |
| Break | ISO527-2/50 | 55.0 | Mpa | |
| Tensile strain | Yield | ISO527-2/50 | 4.0 | % |
| Break | ISO527-2/50 | 10 | % | |
| Tensile modulus | ISO527-2/1 | 2500 | Mpa | |
| Elongation rate 4 | Break | ASTMD638 | 7.0 | % |
| Yield | ASTMD638 | 5.0 | % | |
| Bending modulus 5 | 50.0mmSpan | ASTMD790 | 2550 | Mpa |
| FlexuralStrength5 | Yield,50.0mmSpan | ASTMD790 | 105 | Mpa |
| Tensile strength 4 | Yield | ASTMD638 | 70.0 | Mpa |
| Bending strength 6,7 | ISO178 | 110 | Mpa | |
| Tensile modulus 3 | ASTMD638 | 2500 | Mpa | |
| Tensile strength 4 | Break | ASTMD638 | 60.0 | Mpa |
| Bending modulus 6 | ISO178 | 2400 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature 10 | 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 140 | °C |
| 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 130 | °C | |
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 135 | °C |
| Vicat softening temperature | ASTMD152511 | 155 | °C | |
| -- | ISO306/A50 | 160 | °C | |
| -- | ISO306/B50 | 145 | °C | |
| -- | ISO306/B120 | 155 | °C | |
| RTIElec | UL746 | 110 | °C | |
| Evolution Calendar intelligent importer | UL746 | 105 | °C | |
| RTIStr | UL746 | 115 | °C | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 7.5E-05 | cm/cm/°C |
| MD：23to80°C | ISO11359-2 | 7E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 7.5E-05 | cm/cm/°C | |
| TD：23to80°C | ISO11359-2 | 9E-05 | cm/cm/°C | |
| thermal conductivity | ISO8302 | 0.27 | W/m/K | |
| BallPressure Test | 125°C | IEC60695-10-2 | Pass | |
| 140°C12 | IEC60695-10-2 | Pass |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | 0.800mm,in Oil | IEC60243-1 | 33 | KV/mm |
| 1.60mm,in Oil | IEC60243-1 | 26 | KV/mm | |
| 3.20mm,in Oil | IEC60243-1 | 16 | KV/mm | |
| Relative permittivity | 50Hz | IEC60250 | 2.80 | |
| 60Hz | IEC60250 | 2.80 | ||
| 1MHz | IEC60250 | 2.70 | ||
| Leakage Trace Index | IEC60112 | 250 | V | |
| Dissipation factor | 50Hz | IEC60250 | 9E-04 | |
| 60Hz | IEC60250 | 9E-04 | ||
| 1MHz | IEC60250 | 3E-03 | ||
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC60093 | 1E+15 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 50.0 | J |
| Suspended wall beam gap impact strength 9 | -30°C | ISO180/1A | 5.0 | kJ/m² |
| 23°C | ISO180/1A | 13 | kJ/m² | |
| Impact strength of simply supported beam gap 8 | -30°C | ISO179/1eA | 5.0 | kJ/m² |
| 23°C | ISO179/1eA | 14 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | H358/30 | ISO2039-1 | 113 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | V-0 | |
| 2.0mm | UL94 | 5VA | ||
| Burning wire flammability index | 1.0mm | IEC60695-2-12 | 960 | °C |
| Hot filament ignition temperature | 1.0mm | IEC60695-2-13 | 775 | °C |
| 2.0mm | IEC60695-2-13 | 775 | °C | |
| 3.0mm | IEC60695-2-13 | 775 | °C | |
| Extreme Oxygen Index | ISO4589-2 | 32 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.