| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Density/specific gravity | | ASTMD792 | 1.29 | g/cm³ |
| Melt mass flow rate | 365°C/5.0kg | ASTMD1238 | 20to28 | g/10min |
| Shrinkage rate | MD：3.18mm | ASTMD955 | 0.70 | % |
| Water absorption rate | 24hr | ASTMD570 | 0.37 | % |
| Water absorption rate | Equilibrium | ASTMD570 | 1.1 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | 3.18mm | ASTMD638 | 2340 | Mpa |
| tensile strength | 3.18mm | ASTMD638 | 69.6 | Mpa |
| elongation | Yield,3.18mm | ASTMD638 | 7.2 | % |
| elongation | Break,3.18mm | ASTMD638 | 60to120 | % |
| Bending modulus | 3.17mm | ASTMD790 | 2410 | Mpa |
| Flexural Strength | 5.0%Strain,3.18mm | ASTMD790 | 91.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 1.8MPa,Unannealed,3.18mm | ASTMD648 | 207 | °C |
| Glass transition temperature 2 | | DSC | 220 | °C |
| Linear coefficient of thermal expansion | MD：3.18mm | ASTMD696 | 5.6E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| VolumeResistivity | 3.18mm | ASTMD257 | 9E+15 | ohms·cm |
| Dielectric strength | 0.0254mm | ASTMD149 | >200 | KV/mm |
| Dielectric strength | 3.18mm | ASTMD149 | 15 | KV/mm |
| DielectricConstant | 3.18mm,60Hz | ASTMD150 | 3.44 | |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of cantilever beam gap | 3.17mm | ASTMD256 | 690 | J/m |
| TensileImpactStrength | 3.18mm | ASTMD1822 | 399 | kJ/m² |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Refractive index | | ASTMD542 | 1.672 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| FlameRating3 | 0.76mm | UL94 | V-0 | |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|
| SteamSterilization-w/Morpholine4 | | | >1000 | cycles |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.