PBT/ASA Ultradur® S 4090 G4 BK BASF GERMANY

211

Unit Price:
$4236 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
46MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Low warpage Dimensional stability
Application Areas:Connector As for the load-bearing p Applied in fields that re
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Water absorption rate	饱和	ASTMD570	0.40	%
	Water absorption rate	饱和,23°C	ISO62	0.40	%
		Water absorption rate	平衡,50%RH	ASTMD570	0.20	%
		Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ISO62	0.20	%
Shrinkage rate	TD	ISO294-4	0.74	%
Shrinkage rate	Shrinkage rate	MD	ISO294-4	0.43	%
Viscosity value	降低的粘度	ISO1628	105.0	ml/g
Melt volume flow rate	275°C/2.16kg	ISO1133	20.0	cm3/10min
density		ASTMD792	1.39	g/cm³
density	density		ISO1183	1.39	g/cm³

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile strength	断裂,23°C	ASTMD638	100	Mpa
Tensile creep modulus	1000hr	ISO899-1	4700	Mpa
TensileCreepModule	1hr	ISO899-1	5300	Mpa
Tensile modulus	23°C	ISO527-2	6900	Mpa
elongation	断裂,23°C	ASTMD638	2.5	%
Bending modulus	23°C	ISO178	6400	Mpa
Bending modulus	Bending modulus	23°C	ASTMD790	6100	Mpa
bending strength	23°C	ASTMD790	159	Mpa
Tensile stress	断裂,150°C	ISO527-2	32.2	Mpa
	Tensile stress	断裂,-40°C	ISO527-2	160	Mpa
		Tensile stress	断裂,23°C	ISO527-2	100	Mpa
			Tensile stress	断裂,80°C	ISO527-2	68.0	Mpa
			Tensile stress	Tensile stress	断裂,120°C	ISO527-2	42.0	Mpa
Tensile strain	断裂,-40°C	ISO527-2	2.7	%
	Tensile strain	断裂,23°C	ISO527-2	2.5	%
		Tensile strain	断裂,80°C	ISO527-2	4.2	%
			Tensile strain	断裂,120°C	ISO527-2	7.4	%
			Tensile strain	Tensile strain	断裂,150°C	ISO527-2	6.7	%

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	1.8MPa,未退火	ASTMD648	194	°C
	Hot deformation temperature	1.8MPa,未退火	ISO75-2/A	160	°C
		Hot deformation temperature	0.45MPa,未退火	ASTMD648	216	°C
		Hot deformation temperature	Hot deformation temperature	0.45MPa,未退火	ISO75-2/B	205	°C
Melting temperature (DSC)		ISO3146	223	°C
RTIElec	3.0mm	UL746	130	°C
	RTIElec	0.71mm	UL746	130	°C
	RTIElec	RTIElec	1.5mm	UL746	130	°C
Evolution Calendar intelligent importer	3.0mm	UL746	90.0	°C
	Evolution Calendar intelligent importer	0.71mm	UL746	90.0	°C
	Evolution Calendar intelligent importer	Evolution Calendar intelligent importer	1.5mm	UL746	90.0	°C
RTIStr	0.71mm	UL746	130	°C
	RTIStr	1.5mm	UL746	130	°C
	RTIStr	RTIStr	3.0mm	UL746	130	°C
Peak melting temperature		ASTMD3418	223	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Leakage Trace Index		IEC60112	450	V
Surface resistivity		ASTMD257	1E+14	ohms
Surface resistivity	Surface resistivity		IEC60093	1E+14	ohms
Volume resistivity		IEC60093	>1.0E+13	ohms·cm
VolumeResistivity	1.50mm	ASTMD257	>1.0E+13	ohms·cm

Impact performance	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	23°C	ISO179	7.0	kJ/m²
Impact strength of cantilever beam gap	-40°C	ASTMD256	68	J/m
	Impact strength of cantilever beam gap	23°C	ASTMD256	80	J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO180	7.0	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO179	43	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179	55	kJ/m²

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.