ASA/PC GELOY™ HRA222F-GY6G053 SABIC INNOVATIVE NANSHA
250
- Unit Price:
- $3734 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 15MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan Thermal stability
- Application Areas:Lawn garden equipment Home appliance components
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | Saturation, 23°C | ISO 62 | 0.60 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.20 | % | |
| Outdoor applicability | UL 746C | f1 | ||
| Molten Volume Flow Rate (MVR) | 260°C/2.16 kg | ISO 1133 | 13.0 | cm3/10min |
| Shrinkage rate - Flow 2 | 内部方法 | 0.40 到 0.60 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending modulus 6 | ISO 178 | 2510 | Mpa | |
| Bending stress 6, 7 | ISO 178 | 93.0 | Mpa | |
| Tensile modulus | -- 3 | ASTM D638 | 2590 | Mpa |
| -- | ISO 527-2/1 | 2520 | Mpa | |
| elongation | Yield 5 | ASTM D638 | 4.2 | % |
| Yield 4 | ASTM D638 | 4.3 | % | |
| Yield | ISO 527-2/5 | 4.3 | % | |
| Yield | ISO 527-2/50 | 4.4 | % | |
| Break 5 | ASTM D638 | > 100 | % | |
| Break 4 | ASTM D638 | > 100 | % | |
| Break | ISO 527-2/5, ISO 527-2/50 | > 50 | % | |
| Tensile strength | Yield 4 | ASTM D638 | 63.0 | Mpa |
| Yield 5 | ASTM D638 | 59.0 | Mpa | |
| Yield | ISO 527-2/5 | 62.0 | Mpa | |
| Yield | ISO 527-2/50 | 60.0 | Mpa | |
| Break 5 | ASTM D638 | 66.0 | Mpa | |
| Break 4 | ASTM D638 | 56.0 | Mpa | |
| Break | ISO 527-2/5 | 51.0 | Mpa | |
| Break | ISO 527-2/50 | 45.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat softening temperature | -- | ISO 306/A50 | 111 | °C |
| -- | ISO 306/B50 | 102 | °C | |
| -- | ISO 306/B120 | 104 | °C | |
| Ball Pressure Test | 73 to 77°C | IEC 60695-10-2 | 通过 | |
| Linear coefficient of thermal expansion | Flow : -30 to 80°C | ISO 11359-2 | 6.9E-5 | cm/cm/°C |
| Across Flow : -30 to 80°C | ISO 11359-2 | 7.1E-5 | cm/cm/°C | |
| Across Flow : 23 to 80°C | ISO 11359-2 | 7.5E-5 | cm/cm/°C | |
| RTI | UL 746 | 90.0 | °C | |
| RTI Imp | UL 746 | 90.0 | °C | |
| RTI Elec | UL 746 | 90.0 | °C | |
| Hot deformation temperature 10 | 0.45 MPa, Unannealed, 4.00 mm, 100 mm Span | ISO 75-2/Be | 99.0 | °C |
| 1.8 MPa, Unannealed, 4.00 mm, 100 mm Span | ISO 75-2/Ae | 88.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 0 | ||
| Leakage Trace Index | IEC 60112 | 600 | V |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying time | 2.0 到 4.0 | hr | ||
| Temperature at the rear of the barrel | 200 到 230 | °C | ||
| Temperature in the middle of the barrel | 220 到 260 | °C | ||
| Temperature at the front of the material cylinder | 230 到 270 | °C | ||
| Spray nozzle temperature | 220 到 260 | °C | ||
| drying temperature | 80 到 90 | °C | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Processing (melt) temperature | 230 到 270 | °C | ||
| Mold temperature | 50 到 70 | °C | ||
| Hopper temperature | 60 到 80 | °C |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Extreme Oxygen Index | ISO 4589-2 | 29 | % | |
| UL flame retardant rating | 2.0 mm | UL 94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.