ASA/PC GELOY™ XTPMFR10 WH7E256 SABIC INNOVATIVE US
245
- Unit Price:
- $3153 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability Antistatic High mobility
- Application Areas:Electrical applications Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| MeltViscosity | 260°C,1500sec^-1 | ISO11443 | 105 | Pa·s |
| density | ISO1183 | 1.18 | g/cm³ | |
| Melt volume flow rate | 260°C/2.16kg | ISO1133 | 30.0 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | 断裂 | ISO527-2/5 | 46.0 | Mpa |
| 断裂 | ISO527-2/50 | 47.0 | Mpa | |
| Tensile modulus | ASTMD638 | 2680 | Mpa | |
| ISO527-2/1 | 2680 | Mpa | ||
| Tensile strength | 屈服 | ASTMD638 | 60.0 | Mpa |
| 屈服 | ASTMD638 | 65.0 | Mpa | |
| elongation | 屈服 | ASTMD638 | 4.0 | % |
| Tensile strain | 屈服 | ISO527-2/5 | 4.0 | % |
| 屈服 | ISO527-2/50 | 4.0 | % | |
| elongation | 断裂3 | ASTMD638 | 58 | % |
| 断裂4 | ASTMD638 | 31 | % | |
| Tensile strain | 断裂 | ISO527-2/5 | 50 | % |
| 断裂 | ISO527-2/50 | 21 | % | |
| Bending modulus | ISO178 | 2730 | Mpa | |
| Tensile stress | 屈服 | ISO527-2/5 | 61.0 | Mpa |
| 屈服 | ISO527-2/50 | 66.0 | Mpa | |
| Tensile strength | 断裂3 | ASTMD638 | 49.0 | Mpa |
| 断裂4 | ASTMD638 | 47.0 | Mpa | |
| bending strength | ISO178 | 97.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 90.0 | °C |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 81.0 | °C | |
| Vicat softening temperature | -- | ISO306/B50 | 96.0 | °C |
| -- | ISO306/B120 | 98.0 | °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ISO11359-2 | 6.3E-05 | cm/cm/°C |
| TD：-40到40°C | ISO11359-2 | 6.3E-05 | cm/cm/°C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 13 | kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ASTMD256 | 90 | J/m |
| 23°C | ASTMD256 | 330 | J/m | |
| 0°C | ISO180/1A | 12 | kJ/m² | |
| 23°C | ISO180/1A | 13 | kJ/m² | |
| Multi axis Instrumented Impact Energy | ISO6603-2 | 85.0 | J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.