ASA/PC GELOY™ XP4034 WH8B108 SABIC INNOVATIVE US

242

Unit Price:
$3188 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Thermal stability High mobility Antistatic Weather resistance
Application Areas:Automotive sector
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Melt flow rate	220°C/10.0 kg	ASTM D1238	5.0	g/10 min
	Melt flow rate	260°C/5.0 kg	ASTM D1238	14	g/10 min
	Melt flow rate	Melt flow rate	280°C/3.8 kg	ASTM D1238	24	g/10 min
Shrinkage rate	Flow : 3.20 mm	内部方法	0.50 到 0.70	%
Shrinkage rate	Shrinkage rate	Across Flow : 3.20 mm	内部方法	0.50 到 0.70	%
Water absorption rate	24 hr	ASTM D570	0.25	%
Outdoor applicability		UL 746C	f2

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus		ISO 527-2/1	2500	Mpa
Tensile strength	Yield 2	ASTM D638	62.0	Mpa
	Tensile strength	Yield	ISO 527-2/50	57.0	Mpa
	Tensile strength	Tensile strength	Break	ISO 527-2/50	50.0	Mpa
Tensile strain	Yield	ISO 527-2/50	4.5	%
	Tensile strain	Break 2	ASTM D638	25	%
	Tensile strain	Tensile strain	Break	ISO 527-2/50	130	%
Bending modulus	50.0 mm Span 3	ASTM D790	2510	Mpa
Bending modulus	Bending modulus	-- 4	ISO 178	2500	Mpa
Bending stress	-- 4, 5	ISO 178	75.0	Mpa
Bending stress	Bending stress	Yield, 50.0 mm Span 3	ASTM D790	88.0	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Thermal deformation temperature under load	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	115	°C
	Thermal deformation temperature under load	0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span 7	ISO 75-2/Bf	116	°C
		Thermal deformation temperature under load	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	104	°C
		Thermal deformation temperature under load	Thermal deformation temperature under load	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 7	ISO 75-2/Af	98.0	°C
Vicat softening temperature		ISO 306/B50	113	°C
Linear coefficient of thermal expansion	Flow : -20 to 150°C	ASTM E831	7.2E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -20 to 150°C	ASTM E831	7.2E-5	cm/cm/°C
thermal conductivity		ASTM C177	0.25	W/m/K

injection	Test Result	Unit
drying temperature	95 到 105	°C
drying time	3.0 到 4.0	hr
Suggested maximum moisture content	0.040	%
Suggested injection volume	40 到 80	%
Temperature at the rear of the barrel	240 到 255	°C
Temperature in the middle of the barrel	245 到 260	°C
Temperature at the front of the material cylinder	250 到 265	°C
Spray nozzle temperature	245 到 265	°C
Processing (melt) temperature	260 到 275	°C
Mold temperature	55 到 70	°C
Back pressure	0.300 到 1.00	Mpa
Screw speed	30 到 80	rpm
Exhaust hole depth	0.038 到 0.076	mm

Impact performance	Test Condition	Test Method	Test Result	Unit
Dart impact equipped with measuring instruments	-30°C, Total Energy	ASTM D3763	30.0	J
Dart impact equipped with measuring instruments	Dart impact equipped with measuring instruments	23°C, Total Energy	ASTM D3763	47.0	J

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	R-Scale	ASTM D785	110

optical performance	Test Condition	Test Method	Test Result	Unit
Gardner glossiness	60°, 无织构	ASTM D523	94

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.5 mm	UL 94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.