ASA/PC GELOY™ HRA170-BR6A1436 SABIC INNOVATIVE US
238
- Unit Price:
- $2827 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Weather resistance heat-resisting High impact resistance
- Application Areas:Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Molten Volume Flow Rate (MVR) | 260°C/5.0 kg | ISO 1133 | 17.0 | cm3/10min |
| Shrinkage rate - Flow 1 | 内部方法 | 0.40 到 0.60 | % | |
| Water absorption rate | Saturation, 23°C | ISO 62 | 0.60 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.20 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2500 | Mpa | |
| Tensile stress | Yield | ISO 527-2/5 | 55.0 | Mpa |
| Yield | ISO 527-2/50 | 62.0 | Mpa | |
| Break | ISO 527-2/5 | 60.0 | Mpa | |
| Break | ISO 527-2/50 | 62.0 | Mpa | |
| Tensile strain | Yield | ISO 527-2/5 | 5.0 | % |
| Yield | ISO 527-2/50 | 4.0 | % | |
| Break | ISO 527-2/5 | 130 | % | |
| Break | ISO 527-2/50 | > 50 | % | |
| Bending modulus 2 | ISO 178 | 2400 | Mpa | |
| Bending stress 2, 3 | ISO 178 | 85.0 | Mpa | |
| Taber abraser | 1000 Cycles, 1000 g, CS-17 Wheel | 内部方法 | 95.0 | mg |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature 6 | 0.45 MPa, Unannealed, 4.00 mm, 100 mm Span | ISO 75-2/Be | 121 | °C |
| 1.8 MPa, Unannealed, 4.00 mm, 100 mm Span | ISO 75-2/Ae | 112 | °C | |
| Vicat softening temperature | -- | ISO 306/B50 | 129 | °C |
| -- | ISO 306/B120 | 132 | °C | |
| Linear coefficient of thermal expansion - flow | 23 to 60°C | ISO 11359-2 | 8.0E-5 | cm/cm/°C |
| thermal conductivity | ISO 8302 | 0.20 | W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC 60093 | > 1.0E+15 | ohms | |
| Volume resistivity | IEC 60093 | > 1.0E+15 | ohms·cm | |
| Dielectric strength | 3.20 mm, in Oil | IEC 60243-1 | 17 | KV/mm |
| Relative permittivity | 1 MHz | IEC 60250 | 2.80 | |
| Dissipation factor | 1 MHz | IEC 60250 | 0.013 | |
| Leakage Trace Index | IEC 60112 | 225 | V |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 100 到 110 | °C | ||
| drying time | 2.0 到 4.0 | hr | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Hopper temperature | 60 到 80 | °C | ||
| Temperature at the rear of the barrel | 230 到 260 | °C | ||
| Temperature in the middle of the barrel | 250 到 290 | °C | ||
| Temperature at the front of the material cylinder | 250 到 290 | °C | ||
| Spray nozzle temperature | 240 到 280 | °C | ||
| Processing (melt) temperature | 260 到 290 | °C | ||
| Mold temperature | 60 到 90 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam gap 4 | -30°C | ISO 179/1eA | 12 | kJ/m² |
| 23°C | ISO 179/1eA | 60 | kJ/m² | |
| Suspended wall beam gap impact strength 5 | -30°C | ISO 180/1A | 15 | kJ/m² |
| 23°C | ISO 180/1A | 45 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R -Sale | ISO 2039-2 | 120 | |
| Ball pressure hardness | H 358/30 | ISO 2039-1 | 106 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.6 mm, Testing by SABIC | UL 94 | HB | |
| Burning wire flammability index | 3.2 mm | IEC 60695-2-12 | 750 | °C |
| Extreme Oxygen Index | ISO 4589-2 | 22 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.