PC/PBT LNP™ COLORCOMP™ 6370-BK1G425L SABIC INNOVATIVE US
113
- Unit Price:
- $3631 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 23MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Impact resistant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Specific volume | ASTMD792 | 0.700 | cm³/g | |
| Melt mass flow rate | 250°C/5.0kg | ASTMD1238 | 24 | g/10min |
| Melt volume flow rate | 250°C/5.0kg | ISO1133 | 12.0 | cm3/10min |
| 265°C/5.0kg | ISO1133 | 19.0 | cm3/10min | |
| Shrinkage rate | MD：--2 | 内部方法 | 0.30to0.40 | % |
| MD：--3 | 内部方法 | 0.40to0.50 | % | |
| TD：--2 | 内部方法 | 0.40to0.70 | % | |
| TD：--3 | 内部方法 | 0.70to0.90 | % | |
| Water absorption rate | 24hr | ASTMD570 | 0.090 | % |
| Saturation,23°C | ISO62 | 0.50 | % | |
| Equilibrium,23°C,50%RH | ISO62 | 0.15 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus 4 | ASTMD638 | 9750 | Mpa | |
| Tensile modulus | ISO527-2/1 | 8500 | Mpa | |
| Tensile strength 6 | Yield | ASTMD638 | 97.0 | Mpa |
| Tensile stress | Yield | ISO527-2/5 | 105 | Mpa |
| Tensile strength 5 | Break | ASTMD638 | 91.0 | Mpa |
| Tensile stress | Break | ISO527-2/5 | 3.00 | Mpa |
| Tensile strain 5 | Yield | ASTMD638 | 3.0 | % |
| Tensile strain | Yield | ISO527-2/5 | 3.0 | % |
| Tensile strain 5 | Break | ASTMD638 | 4.0 | % |
| Tensile strain | Break | ISO527-2/5 | 110 | % |
| Bending modulus 7 | 50.0mmSpan | ASTMD790 | 5380 | Mpa |
| ISO178 | 7750 | Mpa | ||
| Bending strength 7,8 | ISO178 | 154 | Mpa | |
| Bending strength 7 | Yield,50.0mmSpan | ASTMD790 | 150 | Mpa |
| FlexuralStrength6 | Break,50.0mmSpan | ASTMD790 | 138 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 163 | °C |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 149 | °C | |
| Hot deformation temperature 11 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 155 | °C |
| Vicat softening temperature | ASTMD152512 | 153 | °C | |
| -- | ISO306/B50 | 148 | °C | |
| -- | ISO306/B120 | 150 | °C | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 2.7E-05 | cm/cm/°C |
| MD：60to138°C | ASTME831 | 2E-05 | cm/cm/°C | |
| MD：-40to40°C | ISO11359-2 | 2.7E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 1.1E-04 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 1.1E-04 | cm/cm/°C | |
| RTIElec | UL746 | 140 | °C | |
| Evolution Calendar intelligent importer | UL746 | 130 | °C | |
| RTIStr | UL746 | 140 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 204 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | 3.20mm,inAir | ASTMD149 | 20 | KV/mm |
| Dielectric constant | 100Hz | ASTMD150 | 4.00 | |
| 1MHz | ASTMD150 | 4.00 | ||
| Dissipation factor | 100Hz | ASTMD150 | 3E-03 | |
| 1MHz | ASTMD150 | 0.020 | ||
| Arc resistance 13 | ASTMD495 | PLC5 | ||
| Compared to the anti leakage trace index | CTI | UL746 | PLC2 | |
| High arc combustion index | HAI | UL746 | PLC3 | |
| High voltage arc tracing rate | HVTR | UL746 | PLC1 | |
| Hot wire ignition | HWI | UL746 | PLC1 | |
| Volume resistivity | ASTMD257 | 4.8E+15 | ohms·cm | |
| Dielectric strength | 1.60mm,in Oil | ASTMD149 | 27 | KV/mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| CharpyNotchedImpactStrength9 | 23°C | ISO179/1eA | 9.0 | kJ/m² |
| Suspended wall beam gap impact strength 10 | -30°C | ISO180/1A | 6.0 | kJ/m² |
| 23°C | ISO180/1A | 10 | kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C,EnergyatPeakLoad | ASTMD3763 | 5.00 | J |
| 23°C,TotalEnergy | ASTMD3763 | 17.0 | J |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ASTMD785 | 109 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.