PC/PBT XENOY™ 1760T SABIC INNOVATIVE US
129
- Unit Price:
- $3276 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 33MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Chemical resistance High mobility Glass fiber reinforced High impact resistance Filler: Glass fiber reinf 11% filler by weight
- Application Areas:Handle Automotive External Parts Shell
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD1 | 内部方法 | 0.50到0.90 | % |
| Water absorption rate | Saturation,23°C | ISO62 | 0.50 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.15 | % | |
| Melt volume flow rate | 250°C/5.0kg | ISO1133 | 14.0 | cm3/10min |
| Density/specific gravity | ISO1183 | 1.30 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending stress 3 | ISO178 | 140 | Mpa | |
| Tensile stress | Break | ISO527-2/5 | 90.0 | Mpa |
| Tensile strain | Break | ISO527-2/5 | 3.0 | % |
| Tensile modulus | ISO527-2/1 | 4500 | Mpa | |
| Bending modulus 2 | ISO178 | 4000 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | MD:23to80°C | ISO11359-2 | 4E-05 | cm/cm/°C |
| TD:23to80°C | ISO11359-2 | 1.1E-04 | cm/cm/°C | |
| thermal conductivity | ISO8302 | 0.19 | W/m/K | |
| BallPressure Test | 75°C | IEC60695-10-2 | Pass | |
| -- | ISO306/B50 | 135 | °C | |
| ISO306/B120 | 130 | °C | ||
| 0.45MPa, unannealed, 100mm span | ISO75-2/Be | 115 | °C | |
| 1.8MPa, unannealed, 100mm span | ISO75-2/Ae | 105 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+14 | ohms·cm | |
| Dielectric strength | 3.20mm,in Oil | IEC60243-1 | 17 | KV/mm |
| Relative permittivity | 50Hz | IEC60250 | 3.30 | |
| 60Hz | IEC60250 | 3.30 | ||
| 1MHz | IEC60250 | 3.10 | ||
| Dissipation factor | 50Hz | IEC60250 | 2E-03 | |
| 60Hz | IEC60250 | 2E-03 | ||
| 1MHz | IEC60250 | 0.020 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Simply supported beam without notch impact strength 5 | -30°C | ISO179/1eU | 35 | kJ/m² |
| 23°C | ISO179/1eU | 35 | kJ/m² | |
| Suspended wall beam notch impact strength 6 | -30°C | ISO180/1A | 3.0 | kJ/m² |
| 0°C | ISO180/1A | 3.0 | kJ/m² | |
| 23°C | ISO180/1A | 3.0 | kJ/m² | |
| Unscented Izod Impact Strength 7 | -30°C | ISO180/1U | 30 | kJ/m² |
| 23°C | ISO180/1U | 30 | kJ/m² | |
| Impact strength of simply supported beam gap 4 | -30°C | ISO179/1eA | 3.5 | kJ/m² |
| 23°C | ISO179/1eA | 4.0 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Sale | ISO2039-2 | 113 | |
| Ball pressure hardness | H358/30 | ISO2039-1 | 105 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.50mm,TestingbySABIC | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.