Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Density/specific gravity | | ASTMD792 | 1.23 | g/cm³ |
| Shrinkage rate | MD | ASTMD955 | 0.20to0.50 | % |
| Water absorption rate | 24hr | ASTMD570 | 0.13 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength 2 | Yield | ASTMD638 | 45.0 | Mpa |
| Tensile stress | Yield | ISO527-2/50 | 45.0 | Mpa |
| Tensile strength 2 | Break | ASTMD638 | 53.0 | Mpa |
| Tensile stress | Break | ISO527-2/50 | 53.0 | Mpa |
| Elongation rate 2 | Yield | ASTMD638 | 5.0 | % |
| Tensile strain | Yield | ISO527-2/50 | 5.0 | % |
| Elongation rate 2 | Break | ASTMD638 | 340 | % |
| Tensile strain | Break | ISO527-2/50 | 340 | % |
| Bending modulus 3 | | ASTMD790 | 1800 | Mpa |
| Bending modulus 3 | | ISO178 | 1800 | Mpa |
| Bending strength 3 | | ASTMD790 | 67.0 | Mpa |
| Bending stress 3 | | ISO178 | 67.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ASTMD648 | 70.0 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed | ASTMD648 | 62.0 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of cantilever beam gap | 23°C | ASTMD256 | NoBreak | |
| Impact strength of cantilever beam gap | 23°C | ISO180 | 130 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | R-Scale | ASTMD785 | 105 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| transmissivity | | ASTMD1003 | 90.0 | % |
| Haze | | ASTMD1003 | <1.0 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| UL flame retardant rating | 3.0mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.