TPEE Hytrel® HYT3078 BK176 DUPONT USA
109
- Unit Price:
- $8073 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Toughening
- Application Areas:Keys
- Color:black
- Grade:Toughened grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | 23°C,24hr | ISO62 | 0.50 | % |
| Saturation,23°C,2.00mm | ISO62 | 0.80 | % | |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.20 | % | |
| Shrinkage rate | TD | ISO294-4 | 0.60 | % |
| MD | ISO294-4 | 0.60 | % | |
| Melt mass flow rate | 190°C/2.16kg | ISO1133 | 5.0 | g/10min |
| MediumDensity | 0.940 | g/cm³ | ||
| SpecificHeatCapacity of Melt | 2150 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.15 | W/m/K | ||
| Melt volume flow rate | 190°C/2.16kg | ISO1133 | 5.00 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2 | 24.0 | Mpa | |
| Bending modulus | ISO178 | 21.0 | Mpa | |
| Tensile stress | Break | ISO527-2 | 24.0 | Mpa |
| 10%Strain | ISO527-2 | 1.80 | Mpa | |
| 50%Strain | ISO527-2 | 5.00 | Mpa | |
| Tensile strain | Break | ISO527-2 | >300 | % |
| Tensile creep modulus | 1000hr | ISO899-1 | 18.0 | Mpa |
| TensileCreepModule | 1hr | ISO899-1 | 22.0 | Mpa |
| Nominal tensile fracture strain | ISO527-2 | 900 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Brittle temperature | ISO974 | -98.0 | °C | |
| Glass transition temperature 2 | ISO11357-2 | -60.0 | °C | |
| EffectiveThermalDiffusivity | 5.44E-08 | m²/s | ||
| Melting temperature 2 | ISO11357-3 | 177 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1.8E-04 | cm/cm/°C |
| TD | ISO11359-2 | 2.1E-04 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | IEC60243-1 | 18 | KV/mm | |
| Relative permittivity | 100Hz | IEC60250 | 5.40 | |
| 1MHz | IEC60250 | 5.30 | ||
| Dissipation factor | 1MHz | IEC60250 | 0.015 | |
| 100Hz | IEC60250 | 7E-03 | ||
| Surface resistivity | IEC60093 | 1E+14 | ohms | |
| Volume resistivity | IEC60093 | 1E+13 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shore hardness | Shore D,15sec | ISO868 | 26 | |
| Shore D | ISO868 | 30 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| 3.0mm | UL94 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| 3.0mm | IEC60695-11-10,-20 | HB | ||
| Extreme Oxygen Index | ISO4589-2 | 19 | % | |
| FMVSS flammability | FMVSS302 | B | ||
| Burning rate 3 | 1.00mm | ISO3795 | <100 | mm/min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.