| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt flow rate | 230°C/2.16 kg | ASTM D1238 | 12 | g/10 min |
| Shrinkage rate - flow | | ASTM D955 | 1.1 | % |
| Water absorption rate | 24 hr, 23°C | ASTM D570 | 0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength | Break, 3.20 mm | ASTM D638 | 25.0 | Mpa |
| elongation | Break, 3.20 mm | ASTM D638 | 860 | % |
| Bending modulus | 3.20 mm | ASTM D790 | 49.0 | Mpa |
| bending strength | 3.20 mm | ASTM D790 | 4.00 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat softening temperature | | ASTM D15253 | 138 | °C |
| Melting peak temperature 4 | | ASTM D3418 | 195 | °C |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|
| drying temperature | | | 100 到 110 | °C |
| drying time | | | 3.0 到 8.0 | hr |
| Suggested maximum moisture content | | | < 0.10 | % |
| Temperature at the rear of the barrel | | | 180 到 190 | °C |
| Temperature in the middle of the barrel | | | 200 到 220 | °C |
| Temperature at the front of the material cylinder | | | 210 到 220 | °C |
| Spray nozzle temperature | | | 210 到 220 | °C |
| Mold temperature | | | 20 到 40 | °C |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore hardness | Shore D | ASTM D2240 | 39 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.8 mm | UL 94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.