TPEE Hytrel® HTR8223 BK320 DUPONT USA
108
- Unit Price:
- $3136 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 50MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan Chemical resistance
- Application Areas:Blow molding applications Cable Automotive Applications
- Color:--
- Grade:Withdrawal level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | 23°C,24hr | ISO62 | 0.60 | % |
| Saturation,23°C,2.00mm | ISO62 | 0.80 | % | |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.20 | % | |
| Shrinkage rate | TD | ISO294-4 | 1.6 | % |
| MD | ISO294-4 | 1.6 | % | |
| Melt mass flow rate | 230°C/10.0kg | ISO1133 | 9.5 | g/10min |
| MediumDensity | 0.980 | g/cm³ | ||
| Melt volume flow rate | 230°C/10.0kg | ISO1133 | 10.0 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Nominal tensile fracture strain | ISO527-2 | 680 | % | |
| abrasion resistance | ISO4649 | 22.0 | mm³ | |
| Tensile modulus | ISO527-2 | 75.0 | Mpa | |
| Bending modulus | ISO178 | 79.0 | Mpa | |
| Tensile stress | Break | ISO527-2 | 26.0 | Mpa |
| 5.0%Strain | ISO527-2 | 3.50 | Mpa | |
| 10%Strain | ISO527-2 | 5.50 | Mpa | |
| 50%Strain | ISO527-2 | 10.0 | Mpa | |
| 100%Strain | ISO527-2 | 13.0 | Mpa | |
| 300%Strain | ISO527-2 | 19.0 | Mpa | |
| Tensile strain | Break | ISO527-2 | >300 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Brittle temperature | ISO974 | -100 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1.7E-04 | cm/cm/°C |
| TD | ISO11359-2 | 1.7E-04 | cm/cm/°C | |
| Melting temperature 2 | ISO11357-3 | 195 | °C | |
| Glass transition temperature 2 | ISO11357-2 | -50.0 | °C | |
| EffectiveThermalDiffusivity | 5.44E-08 | m²/s |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Leakage Trace Index | IEC60112 | 600 | V | |
| Dielectric strength | IEC60243-1 | 18 | KV/mm | |
| Surface resistivity | IEC60093 | 2E+14 | ohms | |
| Volume resistivity | IEC60093 | 9E+12 | ohms·cm | |
| Dissipation factor | 100Hz | IEC60250 | 7E-03 | |
| 1MHz | IEC60250 | 0.013 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shore hardness | Shore D | ISO868 | 42 | |
| Shore D,15sec | ISO868 | 38 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FMVSS flammability | FMVSS302 | B | ||
| Burning rate 3 | 1.00mm | ISO3795 | <100 | mm/min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.