TPEE Hytrel® 4068 DUPONT USA

242

Unit Price:
$12393 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Thermal stability Aging resistance
Application Areas:medical care Lighting fixtures
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Melt mass flow rate	220°C/2.16kg	ISO1133	8.5	g/10min
MediumDensity			1.03	g/cm³
SpecificHeatCapacity of Melt			2140	J/kg/°C
ThermalConductivityofMelt			0.16	W/m/K
Melt volume flow rate	220°C/2.16kg	ISO1133	8.80	cm3/10min
Shrinkage rate	TD	ISO294-4	0.80	%
Shrinkage rate	Shrinkage rate	MD	ISO294-4	0.80	%
Water absorption rate	23°C,24hr	ISO62	0.70	%
	Water absorption rate	Saturation,23°C,2.00mm	ISO62	0.70	%
	Water absorption rate	Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO62	0.30	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus		ISO527-2	45.0	Mpa
Tensile stress	Break	ISO527-2	29.0	Mpa
	Tensile stress	5.0%Strain	ISO527-2	2.40	Mpa
		Tensile stress	10%Strain	ISO527-2	3.20	Mpa
			Tensile stress	50%Strain	ISO527-2	6.70	Mpa
			Tensile stress	Tensile stress	100%Strain	ISO527-2	7.50	Mpa
Tensile strain	Break	ISO527-2	>300	%
Nominal tensile fracture strain		ISO527-2	800	%
TensileCreepModule	1hr	ISO899-1	28.0	Mpa
Tensile creep modulus	1000hr	ISO899-1	21.0	Mpa
Bending modulus		ISO178	45.0	Mpa
abrasion resistance		ISO4649	180	mm³

Thermal performance	Test Condition	Test Method	Test Result	Unit
Melting temperature 2		ISO11357-3	193	°C
Linear coefficient of thermal expansion	MD	ISO11359-2	2.3E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO11359-2	2.3E-04	cm/cm/°C
EffectiveThermalDiffusivity			5.44E-08	m²/s
Glass transition temperature 2		ISO11357-2	-55.0	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric strength		IEC60243-1	18	KV/mm
Relative permittivity	100Hz	IEC60250	4.80
Relative permittivity	Relative permittivity	1MHz	IEC60250	4.70
Leakage Trace Index		IEC60112	600	V

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	NoBreak
Tensile impact strength	23°C	ISO8256/1	145	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Shore hardness	Shore D	ISO868	37
Shore hardness	Shore hardness	Shore D,15sec	ISO868	33

flammability	Test Condition	Test Method	Test Result	Unit
Burning rate 3	1.00mm	ISO3795	<100	mm/min
FMVSS flammability		FMVSS302	B

Supplementary Information	Test Condition	Test Method	Test Result	Unit
EmissionofOrganicCompounds		VDA277	10.0	µgC/g
Odor		VDA270	4.00

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.