TPEE Hytrel® 4556 DUPONT USA
213
- Unit Price:
- $10251 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:UV resistance Thermal stability
- Application Areas:Electrical applications Automotive Applications
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.20 | % |
| Density/specific gravity | ISO1183 | 1.14 | g/cm³ | |
| Melt mass flow rate | 220°C/2.16kg | ISO1133 | 8.5 | g/10min |
| Melt volume flow rate | 220°C/2.16kg | ISO1133 | 7.50 | cm3/10min |
| Shrinkage rate | TD | ISO294-4 | 1.1 | % |
| MD | ISO294-4 | 1.1 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.60 | % |
| Saturation,23°C,2.00mm | ISO62 | 0.60 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| abrasion resistance | ISO4649 | 130 | mm³ | |
| Tensile modulus | ISO527-2 | 85.0 | Mpa | |
| Tensile stress | Break | ISO527-2 | 34.0 | Mpa |
| 10%Strain | ISO527-2 | 5.70 | Mpa | |
| 50%Strain | ISO527-2 | 9.80 | Mpa | |
| 100%Strain | ISO527-2 | 11.0 | Mpa | |
| 300%Strain | ISO527-2 | 17.0 | Mpa | |
| Tensile strain | Break | ISO527-2 | >300 | % |
| Nominal tensile fracture strain | ISO527-2 | 740 | % | |
| Bending modulus | ISO178 | 87.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melting temperature 2 | ISO11357-3 | 193 | °C | |
| Linear coefficient of thermal expansion | MD：-- | ISO11359-2 | 1.7E-04 | cm/cm/°C |
| MD：-40to23°C | ISO11359-2 | 2.2E-04 | cm/cm/°C | |
| TD：-- | ISO11359-2 | 1.9E-04 | cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 2.1E-04 | cm/cm/°C | |
| TD：EffectiveThermalDiffusivity | ISO11359-2 | 5.44E-08 | m²/s | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 50.0 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 35.0 | °C | |
| Brittle temperature | ISO974 | -100 | °C | |
| Glass transition temperature 2 | ISO11357-2 | -45.0 | °C | |
| Vicat softening temperature | -- | ISO306/A50 | 155 | °C |
| -- | ISO306/B50 | 60.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Relative permittivity | 1MHz | IEC60250 | 4.50 | |
| Dissipation factor | 100Hz | IEC60250 | 9.5E-03 | |
| 1MHz | IEC60250 | 0.030 | ||
| Leakage Trace Index | IEC60112 | 600 | V | |
| Surface resistivity | IEC60093 | 4E+14 | ohms | |
| Volume resistivity | IEC60093 | 8E+12 | ohms·cm | |
| Dielectric strength | IEC60243-1 | 19 | KV/mm | |
| Relative permittivity | 100Hz | IEC60250 | 4.80 |
| elastomer | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tear strength | Across Flow | ISO34-1 | 120 | kN/m |
| 流量 | ISO34-1 | 120 | kN/m |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| WaterVaporTransmission Rate | 23°C,85%RH,25µm | DIS15106-1/-2 | 600 | g/m²/24hr |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -40°C | ISO179/1eA | NoBreak | |
| -30°C | ISO179/1eA | NoBreak | ||
| 23°C | ISO179/1eA | NoBreak | ||
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak | ||
| Impact strength of cantilever beam gap | -40°C | ISO180/1A | NoBreak | |
| 23°C | ISO180/1A | NoBreak |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shore hardness | Shore D | ISO868 | 45 | |
| Shore D,15sec | ISO868 | 42 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FMVSS flammability | FMVSS302 | B | ||
| Burning rate 3 | 1.00mm | ISO3795 | <100 | mm/min |
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| 3.0mm | UL94 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| 3.0mm | IEC60695-11-10,-20 | HB | ||
| Extreme Oxygen Index | ISO4589-2 | 20 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.