TPEE Hytrel® 6356 DUPONT GERMANY
153
- Unit Price:
- $4740 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability
- Application Areas:Electrical tools Cable Applications Electrical appliances Electric wire Industrial applications Pipeline components sheet Automotive sector Filamentous
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 1.5 | % |
| MD | ISO294-4 | 1.5 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.50 | % |
| Saturation,23°C,2.00mm | ISO62 | 0.60 | % | |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.20 | % | |
| Melt mass flow rate | 230°C/2.16kg | ISO1133 | 9.0 | g/10min |
| MediumDensity | 1.06 | g/cm³ | ||
| SpecificHeatCapacity of Melt | 2150 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.15 | W/m/K | ||
| Melt volume flow rate | 230°C/2.16kg | ISO1133 | 8.50 | cm3/10min |
| Density/specific gravity | ISO1183 | 1.22 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Nominal tensile fracture strain | ISO527-2 | 500 | % | |
| abrasion resistance | ISO4649 | 110 | mm³ | |
| Tensile creep modulus | 1000hr | ISO899-1 | 182 | Mpa |
| TensileCreepModule | 1hr | ISO899-1 | 248 | Mpa |
| Tensile stress | Yield | ISO527-2 | 20.0 | Mpa |
| Break | ISO527-2 | 43.0 | Mpa | |
| 5.0%Strain | ISO527-2 | 12.0 | Mpa | |
| 10%Strain | ISO527-2 | 15.0 | Mpa | |
| 50%Strain | ISO527-2 | 18.8 | Mpa | |
| 100%Strain | ISO527-2 | 19.0 | Mpa | |
| Tensile strain | Yield | ISO527-2 | 31 | % |
| Break | ISO527-2 | >300 | % | |
| Tensile modulus | ISO527-2 | 280 | Mpa | |
| Bending modulus | ISO178 | 290 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 80.0 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 45.0 | °C | |
| Brittle temperature | ISO974 | -96.0 | °C | |
| Vicat softening temperature | -- | ISO306/A50 | 195 | °C |
| -- | ISO306/B50 | 100 | °C | |
| Melting temperature 2 | ISO11357-3 | 210 | °C | |
| Linear coefficient of thermal expansion | MD：-- | ISO11359-2 | 1.9E-04 | cm/cm/°C |
| MD：-40to23°C | ISO11359-2 | 1.6E-04 | cm/cm/°C | |
| TD：23to55°C | ASTME831 | 1.7E-04 | cm/cm/°C | |
| TD：-- | ISO11359-2 | 1.8E-04 | cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 1.5E-04 | cm/cm/°C | |
| TD：EffectiveThermalDiffusivity | ISO11359-2 | 5.44E-08 | m²/s | |
| Glass transition temperature 2 | ISO11357-2 | 0.00 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Relative permittivity | 100Hz | IEC60250 | 4.60 | |
| 1MHz | IEC60250 | 4.10 | ||
| Dielectric strength | IEC60243-1 | 20 | KV/mm | |
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC60093 | 8E+13 | ohms·cm | |
| Dissipation factor | 100Hz | IEC60250 | 0.012 | |
| 1MHz | IEC60250 | 0.036 |
| elastomer | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tear strength | Across Flow | ISO34-1 | 150 | kN/m |
| 流量 | ISO34-1 | 160 | kN/m |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -40°C | ISO179/1eA | 15 | kJ/m² |
| -30°C | ISO179/1eA | 25 | kJ/m² | |
| 23°C,Partial Break | ISO179/1eA | 120 | kJ/m² | |
| Impact strength of cantilever beam gap | -40°C | ISO180/1A | 19 | kJ/m² |
| 23°C | ISO180/1A | 81 | kJ/m² | |
| Tensile impact strength | 23°C | ISO8256/1 | 300 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shore hardness | Shore D | ISO868 | 63 | |
| Shore D,15sec | ISO868 | 57 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| 3.0mm | UL94 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| 3.0mm | IEC60695-11-10,-20 | HB | ||
| Extreme Oxygen Index | ISO4589-2 | 21 | % | |
| FMVSS flammability | FMVSS302 | SE | ||
| Fogging-G-value | condensate | ISO6452 | 1E-04 | g |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 2.50 | µgC/g | |
| Odor | VDA270 | 2.50 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.