TPEE Hytrel® 4069 DUPONT USA
206
- Unit Price:
- $12040 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:UV resistance Thermal stability
- Application Areas:Electrical applications Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D955 | 1.11 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tear strength | ASTM D-1004 | 95(550) | KN/m(lb/in) | |
| elongation | Break | ASTM D-638 | 700 | % |
| Tensile stress | 张力 10% | ASTM D-638 | 3.5(0.5) | MPa（kpsi） |
| tensile strength | ASTM D412/ISO 527 | 95 | kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 40 | ||
| tear strength | ASTM D624/ISO 34 | 95 | kN/m | |
| Bending modulus | ASTM D790/ISO 178 | 134 | kg/cm²(MPa)[Lb/in²] | |
| Poisson's ratio | ASTM E-132 | 0.45 | ||
| Bending modulus | -40C(-40F) | ASTM D-790 IB | 172(25) | MPa（kpsi） |
| 100C(212F) | ASTM D-790 IB | 28(4.1) | MPa（kpsi） | |
| hardness | ASTM D-2240 | 40 | ||
| Tensile stress | 张力 5% | ASTM D-638 | 2.4(0.4) | MPa（kpsi） |
| Tensile strength at break | ASTM D-638 | 20(2.9) | MPa（kpsi） | |
| Bending modulus | 23C(73F) | ASTM D-790 IB | 55(8.0) | MPa（kpsi） |
| IZOD impact strength | 23C(73F),6.35mm(0.25in) | ASTM D-256-A | NB | J/m(ft lb/in) |
| -40C(-40F),6.35mm(0.25in) | ASTM D-256-A | NB | J/m(ft lb/in) | |
| Tensile elongation at break (elongation at break) | ASTM D412/ISO 527 | 700 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| melting point | 193 | ℃（℉） | ||
| vicat softening point | ASTM D1525/ISO R306 | 134 | ℃（℉） | |
| Hot deformation temperature | 0.45MPa(66psi) | ASTM D-648 | 55(131) | ℃(°F) |
| vicat softening point | ASTM D-1525-B | 134(273) | ℃(°F) | |
| melting point | ASTM D-3418 | 193(379) | ℃(°F) |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt index | 2.16kg at 220C | ASTM D-1238 | 8.5 | g/10min |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Thickness grade | UL 94 | HB | ||
| Thickness testing | UL 94 | 1.56 | mm | |
| density | ASTM D-792 | 1.11 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.