TPEE KOPEL® KP3355 KOLON KOREA

237

Unit Price:
$6222 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet Compare

Physical properties	Test Method	Test Result	Unit
density	ASTM D955	1.19	%
Melt index (flow coefficient)	ASTM D1238/ISO 1133	18	g/10min
Water absorption rate 23 ℃/24h	ASTM D570/ISO 62	0.5	%
Molding shrinkage rate	ASTM D955	1.1-1.3	%

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	TD	ISO294-4	1.4	%
Shrinkage rate	Shrinkage rate	MD	ISO294-4	1.3	%
Water absorption rate	23°C,24hr	ISO62	0.62	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,60%RH	ASTMD570	0.50	%
Melt mass flow rate	220°C/2.16kg	ASTMD1238	25	g/10min
Melt mass flow rate	Melt mass flow rate	220°C/2.16kg	ISO1133	28	g/10min
Shrinkage rate	MD	ASTMD955	1.2	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile strength	Yield,23°C	ASTMD638	30.9	Mpa
Tensile stress	Yield,23°C	ISO527-2	33.0	Mpa
elongation	Yield,23°C	ASTMD638	770	%
Tensile strain	Break,23°C	ISO527-2	700	%
Bending modulus	23°C	ASTMD790	211	Mpa
Bending modulus	Bending modulus	23°C	ISO178	146	Mpa
Tab	1000Cycles,CS-17Wheel	ASTMD1044	5.00	mg
tensile strength		ASTM D412/ISO 527	360	kg/cm²(MPa)[Lb/in²]
Charpy impact strength		ASTM D256/ISO 179	NB	kg·cm/cm(J/M)ft·lb/in
Tensile elongation at break (elongation at break)		ASTM D412/ISO 527	650	%

Thermal performance	Test Condition	Test Method	Test Result	Unit
melting point			200	℃（℉）
Combustibility (rate)		UL94	HB（1.5mm)
Hot deformation temperature	0.45MPa,Unannealed	ASTMD648	102	°C
Brittle temperature		ASTMD746	<-70.0	°C
Vicat softening temperature		ISO306/A50	170	°C
Peak melting temperature		ASTMD3418	200	°C
Melting temperature		ISO11357-3	200	°C

Electrical performance	Test Method	Test Result	Unit
Volume resistivity	IEC60093	1E+15	ohms·cm
Dielectric strength	IEC60243-1	19	KV/mm
Dielectric constant	ASTMD150	4.70
Dissipation factor	ASTMD150	6E-04

hardness	Test Condition	Test Method	Test Result	Unit
Shore hardness	Shore D	ASTMD2240	55
Shore hardness	Shore hardness	Shore D	ISO868	55

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.8mm	UL94	HB

Supplementary Information	Test Condition	Test Method	Test Result	Unit
Resilience			50	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.