PPA AMODEL® AS-4133-BK SOLVAY USA
231
- Unit Price:
- $8373 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 68MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan Filler: Glass fiber reinf 33% filler by weight
- Application Areas:Special material for cast Automotive components Sports equipment
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 23℃ | g/cm³ | 1.29到1.78 | ||
| -- | 1.33到1.73 | |||
| 23℃ | % | 0.14到1.0 | ||
| 23℃,24hr | % | 0.30到0.51 | ||
| Balance, 23 ℃, 50% RH | % | 0.21到1.2 | ||
| Lateral flow: 23 ℃ | mm/mm | 119.4E-3到0.254 | ||
| 23℃,24hr | % | 0.12到0.30 | ||
| Flow: 23 ℃ | mm/mm | 48.3E-3到129.5E-3 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 23℃ | MPa | 5337.93到17586.21 | ||
| MPa | 5200.0到18344.83 | |||
| Fracture, 23 ℃ | MPa | 162.76到199.31 | ||
| Yield, 23 ℃ | % | 1.5到2.6 | ||
| 23℃ | MPa | 88.28到260.0 | ||
| Yield, 23 ℃ | MPa | 12.62到270.34 | ||
| Fracture, 23 ℃ | MPa | 108.28到262.76 | ||
| 23℃ | MPa | 137.93到392.41 | ||
| shear strength | 23℃ | MPa | 88.28到107.59 | |
| 23℃ | MPa | 8827.59到14482.76 | ||
| Yield, 23 ℃ | MPa | 102.76到362.76 | ||
| Poisson's ratio | 23℃ | 0.41 | ||
| compressive strength | 23℃ | MPa | 142.76到196.55 | |
| Yield, 23 ℃ | % | 1.4到2.5 | ||
| 23℃ | MPa | 5137.93到18620.69 | ||
| MPa | 126.21到364.14 | |||
| Fracture, 23 ℃ | % | 1.5到3.1 | ||
| % | 1.0到2.5 | |||
| Tensile modulus | 摩擦系数 | 0.15到0.52 | ||
| Yield, 23 ℃ | MPa | 68.97到250.34 | ||
| Fracture, 23 ℃ | MPa | 131.72到400.0 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| flow | mm/mm/°C | 195.6E-5到25.4E-5 | ||
| -- | °C | 310到312 | ||
| Vicat softening temperature | °C | 258到313 | ||
| Evolution Calendar intelligent importer | °C | 118到150 | ||
| RTIElec | °C | 140到150 | ||
| flow | mm/mm/°C | 38.1E-5到50.8E-5 | ||
| 1.8MPa, unannealed | °C | 249到304 | ||
| flow | mm/mm/°C | 185.4E-5到25.4E-5 | ||
| -- | °C | 299到315 | ||
| 8.0Mpa, unannealed | °C | 165到230 | ||
| 1.8MPa, unannealed | °C | 247到292 | ||
| 0.45MPa, annealed | °C | 296到320 | ||
| 0.45MPa, unannealed | °C | 275到308 | ||
| RTI | °C | 119到150 | ||
| Continuous use temperature | °C | 140到186 | ||
| transverse | mm/mm/°C | 68.6E-5到127.0E-5 | ||
| 1.8MPa, annealed | °C | 283到300 | ||
| transverse | mm/mm/°C | 63.5E-5到177.8E-5 | ||
| 0.45MPa, unannealed | °C | 273到312 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Leakage Trace Index | V | 593到600 | ||
| 23℃ | ohms·cm | 1.0E+3到2.5E+15 | ||
| V/mil | 420到1100 | |||
| ohms·cm | 1.0E+15到2.6E+16 | |||
| 4.9E-3到0.015 | ||||
| 3.66到5.52 | ||||
| 4.0E-3到0.017 | ||||
| -- | ohms | 1.0E+2到2.5E+15 | ||
| 23℃ | V/mil | 450到590 | ||
| 3.66 | ||||
| Compared to the anti leakage trace index | CTI | V | 548到600 | |
| -- | ohms | 1.0E+5到2.5E+16 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 23℃ | J | 0.78到2.04 | ||
| kJ/m² | 0.556到3.158 | |||
| kJ/m² | 4.365到15.786 | |||
| J/m | 0.066到0.351 | |||
| J/m | 0.008到0.042 | |||
| Impact strength of simply supported beam without notch | 23℃ | kJ/m² | 4.178到19.964 | |
| 23℃ | N.m | 138.05到788.50 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | 23℃ | 125 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Extreme Oxygen Index | % | 23到25 | ||
| Burning wire flammability index | °C | 743到960 | ||
| Hot filament ignition temperature | °C | 721到926 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.