PA9T Genestar™ G2330 KURARAY JAPAN
293
- Unit Price:
- $7334 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 110.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan Flame retardant Glass fiber reinforced
- Application Areas:Fiber grade
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.68 | ||
| Molding shrinkage rate | ASTM D955 | 0.1 | % | |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 0.9 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| elongation at break | ASTM D638/ISO 527 | 2.8 | % | |
| tensile strength | ASTM D638/ISO 527 | 175 | kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 125 | ||
| Bending modulus | ASTM D790/ISO 178 | 11000 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 222 | kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638 | 175 | Mpa | |
| elongation | Break | ASTM D638 | 2.8 | % |
| bending strength | ASTM D790 | 222 | Mpa | |
| Bending modulus | ASTM D790 | 11000 | Mpa | |
| Lzod impact strength | ASTM D256 | 100 | J/m | |
| Rockwell hardness | ASTM D785 | 125 | R |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Combustibility | UL94 | V-0 | ||
| melting point | 306 | °C | ||
| Glass transition temperature | 125 | °C | ||
| Combustibility (rate) | UL94 | V-0 | ||
| melting point | 306 | ℃（℉） |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Fiberglass content | 33 | % | ||
| density | 1.68 | g/cm | ||
| Water absorption rate | 40 ℃ ， 95 ％相对湿度， 96hr | 0.9 | % | |
| Shrinkage rate | Flow | 0.1 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.