TPV Santoprene™ 203-40 CELANESE USA

166

Unit Price:
$4334 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
17MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:dimensional stability Insulation performance Recyclable materials Electrical performance Superior tear strength Good colorability Ozone resistance Chemical resistance Fatigue resistance
Application Areas:Electrical components Engine hood parts diaphragm Pipe fittings Movable hinge Home appliance components Automotive sector Consumer goods sector Electrical components diaphragm Pipe fittings Movable hinge Home appliance components Parts under the hood of a Application in the automo Consumer product applicat
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Detergent		ISO188	f4
Detergent	Detergent		UL749	f3

Thermal performance	Test Condition	Test Method	Test Result	Unit
Brittle temperature		ASTMD746	-52.0	°C
Brittle temperature	Brittle temperature		ISO812	-52.0	°C
RTIElec		UL746	85.0	°C
RTIStr		UL746	85.0	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric strength	23°C,2.00mm	ASTMD149	28	KV/mm
DielectricConstant	23°C,1.98mm	ASTMD150	2.30
DielectricConstant	DielectricConstant	23°C,1.98mm	IEC60250	2.30
Compared to the anti leakage trace index	CTI	UL746	PLC0
High arc combustion index	HAI	UL746	PLC0
High voltage arc ignition resistance index	PLC	UL746	PLC5
High voltage arc tracing rate	HVTR	UL746	PLC1
Hot wire ignition (HWI)	1.0mm	UL746	PLC4
	Hot wire ignition (HWI)	1.5mm	UL746	PLC3
	Hot wire ignition (HWI)	Hot wire ignition (HWI)	3.0mm	UL746	PLC2

ageing	Test Condition	Test Method	Test Result	Unit
Quality change rate	23.0°C,168hr,inSodiumHydroxide,50%	ISO1817	0.0	%
	Quality change rate	23.0°C,168hr,inSodiumChloride,15%	ISO1817	0.10	%
		Quality change rate	23.0°C,168hr,inHydrochloricAcid,10%	ISO1817	0.10	%
			Quality change rate	23.0°C,168hr,inSulfuricAcid,98%	ISO1817	1.1	%
				Quality change rate	23.0°C,168hr,inAceticAcid	ISO1817	1.2	%
					Quality change rate	100°C,168hr,inDeionizedWater	ISO1817	1.4	%
						Quality change rate	100°C,168hr,inIRM903Oil	ISO1817	35	%
							Quality change rate	125°C,168hr,inIRM903Oil	ISO1817	44	%
							Quality change rate	Quality change rate	125°C,168hr,inIRM903Oil	ISO1817	44	%
Volume change	125°C,70hr,在IRM903油中	ASTMD471	40	%
	Volume change	125°C,70hr,在IRM903油中	ASTMD471	40	%
		Volume change	125°C,70hr,在IRM903油中	ISO1817	40	%
		Volume change	Volume change	125°C,70hr,在IRM903油中	ISO1817	40	%
Change rate of tensile strength	23°C,168hr,inHydrochloricAcid,10%	ASTMD471	6.0	%
	Change rate of tensile strength	23°C,168hr,inIsopropylAlcohol	ASTMD471	5.0	%
		Change rate of tensile strength	23°C,168hr,inMethylethylketone	ASTMD471	3.0	%
			Change rate of tensile strength	23°C,168hr,inSodiumChloride,15%	ASTMD471	4.0	%
				Change rate of tensile strength	23°C,168hr,inSodiumHydroxide,50%	ASTMD471	4.0	%
					Change rate of tensile strength	23°C,168hr,inSulfuricAcid,98%	ASTMD471	-22	%
						Change rate of tensile strength	23°C,168hr,inTrichloroethylene	ASTMD471	8.0	%
							Change rate of tensile strength	100°C,168hr,inDeionizedWater	ASTMD471	3.0	%
								Change rate of tensile strength	100°C,168hr,inIRM903Oil	ASTMD471	-26	%
								Change rate of tensile strength	Change rate of tensile strength	125°C,70hr,inIRM903Oil	ASTMD471	-27	%
Change rate of hardness of hardness tester 2	ShoreA,23°C,168hr,inMethylethylketone	ASTMD471	0.0
	Change rate of hardness of hardness tester 2	ShoreA,23°C,168hr,inSodiumChloride,15%	ASTMD471	2.0
		Change rate of hardness of hardness tester 2	ShoreA,23°C,168hr,inSodiumHydroxide,50%	ASTMD471	1.0
			Change rate of hardness of hardness tester 2	ShoreA,23°C,168hr,inSulfuricAcid,98%	ASTMD471	2.0
				Change rate of hardness of hardness tester 2	ShoreA,23°C,168hr,inTrichloroethylene	ASTMD471	1.0
					Change rate of hardness of hardness tester 2	ShoreA,100°C,168hr,inDeionizedWater	ASTMD471	0.0
						Change rate of hardness of hardness tester 2	ShoreA,100°C,168hr,inIRM903Oil	ASTMD471	-13
						Change rate of hardness of hardness tester 2	Change rate of hardness of hardness tester 2	ShoreA,125°C,168hr,inIRM903Oil	ASTMD471	-15
ChangeinShoreHardness	ShoreA,23°C,168hr,inAceticAcid	ISO1817	-1.0
ChangeinShoreHardness	ChangeinShoreHardness	ShoreA,23°C,168hr,inCyclohexane	ISO1817	-13
Quality change rate	23°C,168hr,inSulfuricAcid,98%	ASTMD471	1.1	%
	Quality change rate	23°C,168hr,inTrichloroethylene	ASTMD471	-1.0	%
		Quality change rate	100°C,168hr,inDeionizedWater	ASTMD471	1.4	%
			Quality change rate	100°C,168hr,inIRM903Oil	ASTMD471	35	%
				Quality change rate	125°C,168hr,inIRM903Oil	ASTMD471	44	%
				Quality change rate	Quality change rate	23.0°C,168hr,inMethylethylketone	ISO1817	-12	%
Change rate of tensile strength in air	150°C,168hr	ASTMD573	-11	%
Change rate of tensile strength in air	Change rate of tensile strength in air	150°C,168hr	ISO188	-11	%
Change rate of ultimate elongation in air	150°C,168hr	ASTMD573	-15	%
ChangeinDurometerHardnessAir	ShoreD,150°C,168hr	ASTMD573	4.0
ChangeinShoreHardnessinAir	ShoreD,150°C,168hr	ISO188	4.0
Change rate of tensile strength	23°C,168hr,inAceticAcid	ASTMD471	0.0	%
	Change rate of tensile strength	23°C,168hr,inCyclohexane	ASTMD471	-2.0	%
		Change rate of tensile strength	23°C,168hr,inDetergent(Tide),2.5%	ASTMD471	0.0	%
		Change rate of tensile strength	Change rate of tensile strength	23°C,168hr,inEthanol,95%	ASTMD471	-3.0	%
Changes in tensile stress during fracture	100°C,168hr,inDeionizedWater	ISO1817	0.0	%
	Changes in tensile stress during fracture	100°C,168hr,inIRM903Oil	ISO1817	-28	%
		Changes in tensile stress during fracture	125°C,70hr,inIRM903Oil	ISO1817	-33	%
		Changes in tensile stress during fracture	Changes in tensile stress during fracture	125°C,168hr,inIRM903Oil	ISO1817	-39	%
Change rate of hardness of hardness tester 2	ShoreA,23°C,168hr,inAceticAcid	ASTMD471	-1.0
	Change rate of hardness of hardness tester 2	ShoreA,23°C,168hr,inCyclohexane	ASTMD471	-13
		Change rate of hardness of hardness tester 2	ShoreA,23°C,168hr,inDetergent(Tide),2.5%	ASTMD471	0.0
			Change rate of hardness of hardness tester 2	ShoreA,23°C,168hr,inEthanol,95%	ASTMD471	0.0
				Change rate of hardness of hardness tester 2	ShoreA,23°C,168hr,inHydrochloricAcid,10%	ASTMD471	-1.0
				Change rate of hardness of hardness tester 2	Change rate of hardness of hardness tester 2	ShoreA,23°C,168hr,inIsopropylAlcohol	ASTMD471	2.0
Changes in tensile stress during fracture	23°C,168hr,inCyclohexane	ISO1817	2.0	%
	Changes in tensile stress during fracture	23°C,168hr,inDetergent(Tide),2.5%	ISO1817	0.00.0	%
		Changes in tensile stress during fracture	23°C,168hr,inEthanol,95%	ISO1817	-2.0	%
			Changes in tensile stress during fracture	23°C,168hr,inHydrochloricAcid,10%	ISO1817	5.0	%
				Changes in tensile stress during fracture	23°C,168hr,inIsopropylAlcohol	ISO1817	5.0	%
					Changes in tensile stress during fracture	23°C,168hr,inMethylethylketone	ISO1817	2.0	%
						Changes in tensile stress during fracture	23°C,168hr,inSodiumChloride,15%	ISO1817	2.0	%
							Changes in tensile stress during fracture	23°C,168hr,inSodiumHydroxide,50%	ISO1817	3.0	%
								Changes in tensile stress during fracture	23°C,168hr,inSulfuricAcid,98%	ISO1817	-23	%
								Changes in tensile stress during fracture	Changes in tensile stress during fracture	23°C,168hr,inTrichloroethylene	ISO1817	2.0	%
Change rate of tensile strength	125°C,168hr,inIRM903Oil	ASTMD471	-30	%
	Change rate of tensile strength	23°C,168hr,inAceticAcid	ISO1817	0.0	%
		Change rate of tensile strength	23°C,168hr,inCyclohexane	ISO1817	-2.0	%
			Change rate of tensile strength	23°C,168hr,inDetergent(Tide),2.5%	ISO1817	0.0	%
				Change rate of tensile strength	23°C,168hr,inEthanol,95%	ISO1817	-3.0	%
					Change rate of tensile strength	23°C,168hr,inHydrochloricAcid,10%	ISO1817	6.0	%
						Change rate of tensile strength	23°C,168hr,inIsopropylAlcohol	ISO1817	5.0	%
							Change rate of tensile strength	23°C,168hr,inMethylethylketone	ISO1817	3.0	%
								Change rate of tensile strength	23°C,168hr,inSodiumChloride,15%	ISO1817	4.0	%
								Change rate of tensile strength	Change rate of tensile strength	23°C,168hr,inSodiumHydroxide,50%	ISO1817	4.0	%
Change rate of ultimate elongation	23°C,168hr,inIsopropylAlcohol	ASTMD471	5.0	%
	Change rate of ultimate elongation	23°C,168hr,inMethylethylketone	ASTMD471	2.0	%
		Change rate of ultimate elongation	23°C,168hr,inSodiumChloride,15%	ASTMD471	2.0	%
			Change rate of ultimate elongation	23°C,168hr,inSodiumHydroxide,50%	ASTMD471	3.0	%
				Change rate of ultimate elongation	23°C,168hr,inSulfuricAcid,98%	ASTMD471	-23	%
					Change rate of ultimate elongation	23°C,168hr,inTrichloroethylene	ASTMD471	2.0	%
						Change rate of ultimate elongation	100°C,168hr,inDeionizedWater	ASTMD471	0.0	%
							Change rate of ultimate elongation	100°C,168hr,inIRM903Oil	ASTMD471	-28	%
								Change rate of ultimate elongation	125°C,70hr,inIRM903Oil	ASTMD471	-33	%
								Change rate of ultimate elongation	Change rate of ultimate elongation	125°C,168hr,inIRM903Oil	ASTMD471	-39	%
Change rate of tensile strength	23°C,168hr,inSulfuricAcid,98%	ISO1817	-22	%
	Change rate of tensile strength	23°C,168hr,inTrichloroethylene	ISO1817	8.0	%
		Change rate of tensile strength	100°C,168hr,inDeionizedWater	ISO1817	3.0	%
			Change rate of tensile strength	100°C,168hr,inIRM903Oil	ISO1817	-26	%
				Change rate of tensile strength	125°C,70hr,inIRM903Oil	ISO1817	-27	%
				Change rate of tensile strength	Change rate of tensile strength	125°C,168hr,inIRM903Oil	ISO1817	-30	%
Change rate of ultimate elongation	23°C,168hr,inCyclohexane	ASTMD471	2.0	%
	Change rate of ultimate elongation	23°C,168hr,inDetergent(Tide),2.5%	ASTMD471	0.00.0	%
		Change rate of ultimate elongation	23°C,168hr,inEthanol,95%	ASTMD471	-2.0	%
		Change rate of ultimate elongation	Change rate of ultimate elongation	23°C,168hr,inHydrochloricAcid,10%	ASTMD471	5.0	%
ChangeinShoreHardness	ShoreA,23°C,168hr,inDetergent(Tide),2.5%	ISO1817	0.0
	ChangeinShoreHardness	ShoreA,23°C,168hr,inEthanol,95%	ISO1817	0.0
		ChangeinShoreHardness	ShoreA,23°C,168hr,inHydrochloricAcid,10%	ISO1817	-1.0
			ChangeinShoreHardness	ShoreA,23°C,168hr,inIsopropylAlcohol	ISO1817	2.0
				ChangeinShoreHardness	ShoreA,23°C,168hr,inMethylethylketone	ISO1817	0.0
					ChangeinShoreHardness	ShoreA,23°C,168hr,inSodiumChloride,15%	ISO1817	2.0
						ChangeinShoreHardness	ShoreA,23°C,168hr,inSodiumHydroxide,50%	ISO1817	1.0
							ChangeinShoreHardness	ShoreA,23°C,168hr,inSulfuricAcid,98%	ISO1817	2.0
								ChangeinShoreHardness	ShoreA,23°C,168hr,inTrichloroethylene	ISO1817	1.0
								ChangeinShoreHardness	ChangeinShoreHardness	ShoreA,100°C,168hr,inDeionizedWater	ISO1817	0.0
Quality change rate	23.0°C,168hr,inIsopropylAlcohol	ISO1817	-5.0	%
	Quality change rate	23.0°C,168hr,inCyclohexane	ISO1817	-3.4	%
		Quality change rate	23.0°C,168hr,inTrichloroethylene	ISO1817	-1.0	%
		Quality change rate	Quality change rate	23.0°C,168hr,inEthanol,95%	ISO1817	-0.60	%
ChangeinShoreHardness	ShoreA,100°C,168hr,inIRM903Oil	ISO1817	-13
ChangeinShoreHardness	ChangeinShoreHardness	ShoreA,125°C,168hr,inIRM903Oil	ISO1817	-15
Quality change rate	23°C,168hr,inAceticAcid	ASTMD471	1.2	%
	Quality change rate	23°C,168hr,inCyclohexane	ASTMD471	-3.4	%
		Quality change rate	23°C,168hr,inEthanol,95%	ASTMD471	-0.60	%
			Quality change rate	23°C,168hr,inEthanol,95%	ASTMD471	-0.60	%
				Quality change rate	23°C,168hr,inHydrochloricAcid,10%	ASTMD471	0.10	%
					Quality change rate	23°C,168hr,inHydrochloricAcid,10%	ASTMD471	0.10	%
						Quality change rate	23°C,168hr,inIsopropylAlcohol	ASTMD471	-5.0	%
							Quality change rate	23°C,168hr,inMethylethylketone	ASTMD471	-12	%
								Quality change rate	23°C,168hr,inSodiumChloride,15%	ASTMD471	0.10	%
								Quality change rate	Quality change rate	23°C,168hr,inSodiumHydroxide,50%	ASTMD471	0.0	%

elastomer	Test Condition	Test Method	Test Result	Unit
TearStrength-AcrossFlow3	23°C	ISO34-1	67	kN/m
CompressionSet4	70°C,22hr	ASTMD395B	54	%
CompressionSet4	CompressionSet4	125°C,70hr	ASTMD395B	61	%
Compression permanent deformation 4	70°C,22hr	ISO815	54	%
Compression permanent deformation 4	Compression permanent deformation 4	125°C,70hr	ISO815	61	%
Tensile stress transverse flow rate	100%Strain,23°C	ASTMD412	9.00	Mpa
Tensile stress transverse flow rate	Tensile stress transverse flow rate	100%Strain,23°C	ISO37	9.00	Mpa
Tensile strength - transverse flow rate	Break,23°C	ASTMD412	20.7	Mpa
Tensile strength TD	Break,23°C	ISO37	20.7	Mpa
Elongation rate - lateral flow rate	Break,23°C	ASTMD412	610	%
Elongation rate - lateral flow rate	Elongation rate - lateral flow rate	Break,23°C	ISO37	610	%
Tear strength - transverse flow rate 2	23°C	ASTMD624	67.0	kN/m

hardness	Test Condition	Test Method	Test Result	Unit
Shore hardness	Shore D,15sec,23°C	ISO868	41

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.0mm	UL94	HB
	UL flame retardant rating	1.5mm	UL94	HB
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.