TPV Santoprene™ 101-73 CELANESE USA

234

Unit Price:
$4428 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
124MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High temperature resistan Aging resistance Flame retardant
Application Areas:Electrical tools Electrical applications Electrical components Washer diaphragm Pipe fittings Home appliance components Seals Parts under the hood of a Application in the automo Automotive Applications Outdoor applications Consumer product applicat
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Outdoor applicability		UL746C	f1
Detergent		ISO188	f4
Detergent	Detergent		UL749	f3

Thermal performance	Test Condition	Test Method	Test Result	Unit
Brittle temperature		ASTMD746	-60.0	°C
Brittle temperature	Brittle temperature		ISO812	-60.0	°C
RTIElec		UL746	90.0	°C
RTIStr	1.0mm	UL746	90.0	°C
	RTIStr	1.5mm	UL746	90.0	°C
	RTIStr	RTIStr	3.0mm	UL746	95.0	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric strength	23°C,2.00mm	ASTMD149	27	KV/mm
DielectricConstant	23°C,1.98mm	ASTMD150	2.50
DielectricConstant	DielectricConstant	23°C,1.98mm	IEC60250	2.50
Compared to the anti leakage trace index	CTI	UL746	PLC0
High arc combustion index	HAI	UL746	PLC0
High voltage arc ignition resistance index	PLC	UL746	PLC6
High voltage arc tracing rate	HVTR	UL746	PLC1
Hot wire ignition (HWI)	1.0mm	UL746	PLC4
	Hot wire ignition (HWI)	1.5mm	UL746	PLC3
	Hot wire ignition (HWI)	Hot wire ignition (HWI)	3.0mm	UL746	PLC3

ageing	Test Condition	Test Method	Test Result	Unit
Change rate of tensile strength	23°C,168hr,inHydrochloricAcid,10%	ISO1817	13	%
	Change rate of tensile strength	23°C,168hr,inIsopropylAlcohol	ISO1817	31	%
		Change rate of tensile strength	23°C,168hr,inMethylethylketone	ISO1817	47	%
			Change rate of tensile strength	23°C,168hr,inSodiumChloride,15%	ISO1817	0.0	%
				Change rate of tensile strength	23°C,168hr,inSodiumHydroxide,50%	ISO1817	3.0	%
					Change rate of tensile strength	23°C,168hr,inSulfuricAcid,98%	ISO1817	-17	%
						Change rate of tensile strength	23°C,168hr,inTrichloroethylene	ISO1817	54	%
							Change rate of tensile strength	100°C,168hr,inDeionizedWater	ISO1817	1.0	%
								Change rate of tensile strength	100°C,168hr,inIRM903Oil	ISO1817	-30	%
								Change rate of tensile strength	Change rate of tensile strength	125°C,70hr,inIRM903Oil	ISO1817	-31	%
Changes in tensile stress during fracture	125°C,168hr,inIRM903Oil	ISO1817	-58	%
Change rate of hardness of hardness tester 2	ShoreA,23°C,168hr,inAceticAcid	ASTMD471	-2.0
	Change rate of hardness of hardness tester 2	ShoreA,23°C,168hr,inCyclohexane	ASTMD471	-16
		Change rate of hardness of hardness tester 2	ShoreA,23°C,168hr,inDetergent(Tide),2.5%	ASTMD471	0.0
			Change rate of hardness of hardness tester 2	ShoreA,23°C,168hr,inEthanol,95%	ASTMD471	0.0
				Change rate of hardness of hardness tester 2	ShoreA,23°C,168hr,inHydrochloricAcid,10%	ASTMD471	-3.0
					Change rate of hardness of hardness tester 2	ShoreA,23°C,168hr,inIsopropylAlcohol	ASTMD471	-1.0
						Change rate of hardness of hardness tester 2	ShoreA,23°C,168hr,inMethylethylketone	ASTMD471	0.0
							Change rate of hardness of hardness tester 2	ShoreA,23°C,168hr,inSodiumChloride,15%	ASTMD471	0.0
							Change rate of hardness of hardness tester 2	Change rate of hardness of hardness tester 2	ShoreA,23°C,168hr,inSodiumHydroxide,50%	ASTMD471	0.0
Change rate of tensile strength in air	150°C,168hr	ASTMD573	-1.0	%
Change rate of tensile strength in air	Change rate of tensile strength in air	150°C,168hr	ISO188	-1.0	%
Change rate of ultimate elongation in air	150°C,168hr	ASTMD573	-3.0	%
ChangeinDurometerHardnessAir	ShoreA,150°C,168hr	ASTMD573	7.0
Change rate of tensile strength	23°C,168hr,inSulfuricAcid,98%	ASTMD471	-17	%
	Change rate of tensile strength	23°C,168hr,inTrichloroethylene	ASTMD471	54	%
		Change rate of tensile strength	100°C,168hr,inDeionizedWater	ASTMD471	1.0	%
			Change rate of tensile strength	100°C,168hr,inIRM903Oil	ASTMD471	-30	%
				Change rate of tensile strength	125°C,70hr,inIRM903Oil	ASTMD471	-31	%
					Change rate of tensile strength	125°C,168hr,inIRM903Oil	ASTMD471	-31	%
						Change rate of tensile strength	23°C,168hr,inAceticAcid	ISO1817	-8.0	%
							Change rate of tensile strength	23°C,168hr,inCyclohexane	ISO1817	31	%
								Change rate of tensile strength	23°C,168hr,inDetergent(Tide),2.5%	ISO1817	3.0	%
									Change rate of tensile strength	23°C,168hr,inEthanol,95%	ISO1817	-2.0	%
									Change rate of tensile strength	Change rate of tensile strength	125°C,168hr,inIRM903Oil	ISO1817	-31	%
Change rate of ultimate elongation	23°C,168hr,inAceticAcid	ASTMD471	-4.0	%
	Change rate of ultimate elongation	23°C,168hr,inCyclohexane	ASTMD471	20	%
		Change rate of ultimate elongation	23°C,168hr,inDetergent(Tide),2.5%	ASTMD471	2.0	%
			Change rate of ultimate elongation	23°C,168hr,inEthanol,95%	ASTMD471	0.0	%
				Change rate of ultimate elongation	23°C,168hr,inHydrochloricAcid,10%	ASTMD471	9.0	%
					Change rate of ultimate elongation	23°C,168hr,inIsopropylAlcohol	ASTMD471	20	%
						Change rate of ultimate elongation	23°C,168hr,inMethylethylketone	ASTMD471	24	%
							Change rate of ultimate elongation	23°C,168hr,inSodiumChloride,15%	ASTMD471	-2.0	%
							Change rate of ultimate elongation	Change rate of ultimate elongation	23°C,168hr,inSodiumHydroxide,50%	ASTMD471	2.0	%
Change rate of hardness of hardness tester 2	ShoreA,23°C,168hr,inSulfuricAcid,98%	ASTMD471	0.0
	Change rate of hardness of hardness tester 2	ShoreA,23°C,168hr,inTrichloroethylene	ASTMD471	-3.0
		Change rate of hardness of hardness tester 2	ShoreA,100°C,168hr,inDeionizedWater	ASTMD471	-2.0
			Change rate of hardness of hardness tester 2	ShoreA,100°C,168hr,inIRM903Oil	ASTMD471	-21
			Change rate of hardness of hardness tester 2	Change rate of hardness of hardness tester 2	ShoreA,125°C,168hr,inIRM903Oil	ASTMD471	-23
ChangeinShoreHardness	ShoreA,23°C,168hr,inAceticAcid	ISO1817	-2.0
	ChangeinShoreHardness	ShoreA,23°C,168hr,inCyclohexane	ISO1817	-16
		ChangeinShoreHardness	ShoreA,23°C,168hr,inDetergent(Tide),2.5%	ISO1817	0.0
			ChangeinShoreHardness	ShoreA,23°C,168hr,inEthanol,95%	ISO1817	0.0
			ChangeinShoreHardness	ChangeinShoreHardness	ShoreA,23°C,168hr,inHydrochloricAcid,10%	ISO1817	-3.0
Change rate of ultimate elongation	23°C,168hr,inSulfuricAcid,98%	ASTMD471	-27	%
	Change rate of ultimate elongation	23°C,168hr,inTrichloroethylene	ASTMD471	22	%
		Change rate of ultimate elongation	100°C,168hr,inDeionizedWater	ASTMD471	-7.0	%
			Change rate of ultimate elongation	100°C,168hr,inIRM903Oil	ASTMD471	-49	%
				Change rate of ultimate elongation	125°C,70hr,inIRM903Oil	ASTMD471	-47	%
				Change rate of ultimate elongation	Change rate of ultimate elongation	125°C,168hr,inIRM903Oil	ASTMD471	-58	%
Changes in tensile stress during fracture	23°C,168hr,inAceticAcid	ISO1817	-4.0	%
	Changes in tensile stress during fracture	23°C,168hr,inCyclohexane	ISO1817	20	%
		Changes in tensile stress during fracture	23°C,168hr,inDetergent(Tide),2.5%	ISO1817	2.0	%
		Changes in tensile stress during fracture	Changes in tensile stress during fracture	23°C,168hr,inEthanol,95%	ISO1817	0.0	%
ChangeinShoreHardness	ShoreA,23°C,168hr,inIsopropylAlcohol	ISO1817	-1.0
	ChangeinShoreHardness	ShoreA,23°C,168hr,inMethylethylketone	ISO1817	0.0
		ChangeinShoreHardness	ShoreA,23°C,168hr,inSodiumChloride,15%	ISO1817	0.0
			ChangeinShoreHardness	ShoreA,23°C,168hr,inSodiumHydroxide,50%	ISO1817	0.0
				ChangeinShoreHardness	ShoreA,23°C,168hr,inSulfuricAcid,98%	ISO1817	0.0
					ChangeinShoreHardness	ShoreA,23°C,168hr,inTrichloroethylene	ISO1817	-3.0
						ChangeinShoreHardness	ShoreA,100°C,168hr,inDeionizedWater	ISO1817	-2.0
							ChangeinShoreHardness	ShoreA,100°C,168hr,inIRM903Oil	ISO1817	-21
							ChangeinShoreHardness	ChangeinShoreHardness	ShoreA,125°C,168hr,inIRM903Oil	ISO1817	-23
Quality change rate	23°C,168hr,inAceticAcid	ASTMD471	4.0	%
	Quality change rate	23.0°C,168hr,inSodiumChloride,15%	ISO1817	0.20	%
		Quality change rate	23.0°C,168hr,inDetergent(Tide),2.5%	ISO1817	0.60	%
			Quality change rate	23.0°C,168hr,inSulfuricAcid,98%	ISO1817	3.6	%
				Quality change rate	100°C,168hr,inDeionizedWater	ISO1817	3.6	%
					Quality change rate	23.0°C,168hr,inAceticAcid	ISO1817	4.0	%
						Quality change rate	100°C,168hr,inIRM903Oil	ISO1817	66	%
						Quality change rate	Quality change rate	125°C,168hr,inIRM903Oil	ISO1817	78	%
Volume change	125°C,70hr,在IRM903油中	ASTMD471	72	%
Volume change	Volume change	125°C,70hr,在IRM903油中	ISO1817	72	%
ChangeinShoreHardnessinAir	ShoreA,150°C,168hr	ISO188	7.0
Change rate of tensile strength	23°C,168hr,inAceticAcid	ASTMD471	-8.0	%
	Change rate of tensile strength	23°C,168hr,inCyclohexane	ASTMD471	31	%
		Change rate of tensile strength	23°C,168hr,inDetergent(Tide),2.5%	ASTMD471	3.0	%
			Change rate of tensile strength	23°C,168hr,inEthanol,95%	ASTMD471	-2.0	%
				Change rate of tensile strength	23°C,168hr,inHydrochloricAcid,10%	ASTMD471	13	%
					Change rate of tensile strength	23°C,168hr,inIsopropylAlcohol	ASTMD471	31	%
						Change rate of tensile strength	23°C,168hr,inMethylethylketone	ASTMD471	47	%
							Change rate of tensile strength	23°C,168hr,inSodiumChloride,15%	ASTMD471	0.0	%
							Change rate of tensile strength	Change rate of tensile strength	23°C,168hr,inSodiumHydroxide,50%	ASTMD471	3.0	%
Changes in tensile stress during fracture	23°C,168hr,inHydrochloricAcid,10%	ISO1817	9.0	%
	Changes in tensile stress during fracture	23°C,168hr,inIsopropylAlcohol	ISO1817	20	%
		Changes in tensile stress during fracture	23°C,168hr,inMethylethylketone	ISO1817	24	%
			Changes in tensile stress during fracture	23°C,168hr,inSodiumChloride,15%	ISO1817	-2.0	%
				Changes in tensile stress during fracture	23°C,168hr,inSodiumHydroxide,50%	ISO1817	2.0	%
					Changes in tensile stress during fracture	23°C,168hr,inSulfuricAcid,98%	ISO1817	-27	%
						Changes in tensile stress during fracture	23°C,168hr,inTrichloroethylene	ISO1817	22	%
							Changes in tensile stress during fracture	100°C,168hr,inDeionizedWater	ISO1817	-7.0	%
								Changes in tensile stress during fracture	100°C,168hr,inIRM903Oil	ISO1817	-49	%
								Changes in tensile stress during fracture	Changes in tensile stress during fracture	125°C,70hr,inIRM903Oil	ISO1817	-47	%
Quality change rate	23°C,168hr,inCyclohexane	ASTMD471	-4.9	%
	Quality change rate	23°C,168hr,inDetergent(Tide),2.5%	ASTMD471	0.60	%
		Quality change rate	23°C,168hr,inEthanol,95%	ASTMD471	-0.10	%
			Quality change rate	23°C,168hr,inHydrochloricAcid,10%	ASTMD471	0.20	%
				Quality change rate	23°C,168hr,inIsopropylAlcohol	ASTMD471	-13	%
					Quality change rate	23°C,168hr,inMethylethylketone	ASTMD471	-24	%
						Quality change rate	23°C,168hr,inSodiumChloride,15%	ASTMD471	0.20	%
							Quality change rate	23°C,168hr,inSodiumHydroxide,50%	ASTMD471	-0.20	%
								Quality change rate	23°C,168hr,inSulfuricAcid,98%	ASTMD471	3.6	%
									Quality change rate	23°C,168hr,inTrichloroethylene	ASTMD471	-6.0	%
										Quality change rate	100°C,168hr,inDeionizedWater	ASTMD471	3.6	%
											Quality change rate	100°C,168hr,inIRM903Oil	ASTMD471	66	%
												Quality change rate	125°C,168hr,inIRM903Oil	ASTMD471	78	%
													Quality change rate	23.0°C,168hr,inMethylethylketone	ISO1817	-24	%
														Quality change rate	23.0°C,168hr,inIsopropylAlcohol	ISO1817	-13	%
															Quality change rate	23.0°C,168hr,inTrichloroethylene	ISO1817	-6.0	%
																Quality change rate	23.0°C,168hr,inCyclohexane	ISO1817	-4.9	%
																	Quality change rate	23.0°C,168hr,inSodiumHydroxide,50%	ISO1817	-0.20	%
																		Quality change rate	23.0°C,168hr,inEthanol,95%	ISO1817	-0.10	%
																		Quality change rate	Quality change rate	23.0°C,168hr,inHydrochloricAcid,10%	ISO1817	0.20	%

elastomer	Test Condition	Test Method	Test Result	Unit
Elongation rate - lateral flow rate	Break,23°C	ASTMD412	490	%
Elongation rate - lateral flow rate	Elongation rate - lateral flow rate	Break,23°C	ISO37	490	%
Tear strength - transverse flow rate 2	23°C	ASTMD624	27.0	kN/m
TearStrength-AcrossFlow3	23°C	ISO34-1	27	kN/m
CompressionSet4	70°C,22hr	ASTMD395B	28	%
CompressionSet4	CompressionSet4	125°C,70hr	ASTMD395B	37	%
Compression permanent deformation 4	70°C,22hr	ISO815	28	%
Compression permanent deformation 4	Compression permanent deformation 4	125°C,70hr	ISO815	37	%
Tensile stress transverse flow rate	100%Strain,23°C	ASTMD412	3.60	Mpa
Tensile stress transverse flow rate	Tensile stress transverse flow rate	100%Strain,23°C	ISO37	3.60	Mpa
Tensile strength - transverse flow rate	Break,23°C	ASTMD412	8.80	Mpa
Tensile strength TD	Break,23°C	ISO37	8.80	Mpa

hardness	Test Condition	Test Method	Test Result	Unit
Shore hardness	Shore A,15sec,23°C	ISO868	78

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.0mm	UL94	HB
	UL flame retardant rating	1.5mm	UL94	HB
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.