TPU IROGRAN® A78P4766 HUNTSMAN GERMANY
242
Unit Price:$11140 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 39MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Foggy surface
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt volume flow rate | 190°C/21.6kg | 110 | cm3/10min | |
| Shrinkage rate | MD：Injection | ASTMD955 | 1.0 | % |
| Shore hardness A | ISO 7619 | 80 | Shore A | |
| Shore hardness D | ISO 7619 | 31 | Shore D |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | DIN 53504 | 34 | Mpa | |
| 100% tensile modulus | DIN 53504 | 4.0 | Mpa | |
| 300% tensile modulus | DIN 53504 | 7.0 | Mpa | |
| elongation | Break | DIN 53504 | 670 | % |
| tear strength | ISO 34-1 | 76 | N/mm | |
| abrasion | ISO 4649 | 40 | mm³ | |
| Compression permanent deformation for 24 hours at 23 ℃ | ISO 815 | 24 | % | |
| Compression permanent deformation for 24 hours at 70 ℃ | ISO 815 | 42 | % | |
| Abrasion2 | ISO4649 | 40 | mm³ |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Lower limit of melting temperature range | Huntsman | 127 | °C | |
| Upper limit of melting temperature range | Huntsman | 156 | °C | |
| TMA3 | High:635.0µm | 内部方法 | 190 | °C |
| Low:635.0µm | 内部方法 | 165 | °C |
| elastomer | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress 2 | 100%Strain | ASTMD412 | 5.79 | Mpa |
| 100%Strain | DIN53504 | 5.20 | Mpa | |
| 300%Strain | ASTMD412 | 9.65 | Mpa | |
| 300%Strain | DIN53504 | 8.00 | Mpa | |
| Tensile strength 2 | Break | ASTMD412 | 27.6 | Mpa |
| Tensile stress 2 | Break | DIN53504 | 30.0 | Mpa |
| Elongation rate 2 | Break | ASTMD412 | 800 | % |
| Break | DIN53504 | 800 | % | |
| Tear strength 2 | ASTMD624 | 71.8 | kN/m | |
| ISO34-1 | 40 | kN/m | ||
| Compression permanent deformation 2 | 23°C,24hr | ASTMD395 | 20 | % |
| 70°C,24hr | ASTMD395 | 40 | % | |
| 23°C,24hr | ISO815 | 20 | % | |
| 70°C,24hr | ISO815 | 40 | % |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shore hardness | Shore A,Injection | ASTMD2240 | 82 | |
| Shore D,Injection | ASTMD2240 | 30 | ||
| Shore A,Injection | ISO868 | 82 | ||
| Shore D,Injection | ISO868 | 30 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | UL94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.