TPU Elastollan® C90A BASF GERMANY
166
- Unit Price:
- $9415 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:high strength wear resistant enhance High impact resistance
- Application Areas:Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 210°C/21.6kg | ASTMD1238 | 30到50 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Concave convex impact strength | －30°C | DIN 53453 | 不破裂 | kJ/m² |
| Room temperature compression deformation rate | DIN 53517 | 25 | % | |
| Compression deformation rate | 70°C | DIN 53517 | 40 | % |
| Hardness Xiao style | DIN 53505 | 41 | shoreB | |
| Tensile modulus | 300% | DIN 53504-S2 | 15 | n/mm² |
| Concave convex impact strength | ＋23°C | DIN 53453 | 不破裂 | kJ/m² |
| Tensile modulus | 20% | DIN 53504-S2 | 7 | n/mm² |
| tensile strength | 80℃水中21天 | DIN 53504-S2 | 40 | n/mm² |
| Fracture elongation rate | DIN 53504-S2 | 550 | % | |
| tear strength | DIN 53515 | 95 | N/mm | |
| Friction loss | DIN 53516 | 25 | mm³ | |
| tensile strength | DIN 53504-S2 | 55 | n/mm² | |
| Hardness Xiao style | DIN 53505 | 93 | shoreA | |
| Fracture elongation rate | 80℃水中21天 | DIN 53504-S2 | 550 | % |
| Tensile modulus | 100% | DIN 53504-S2 | 9 | n/mm² |
| 100% modulus | ASTM D412/ISO 527 | 9 | Mpa/Psi | |
| 300% modulus | ASTM D412/ISO 527 | 15 | Mpa/Psi | |
| Tensile strength | ASTM D412/ISO 527 | 55 | Mpa/Psi | |
| tear strength | ASTM D624/ISO 34 | 95 | n/mm² | |
| Hardness A | ASTM D2240/ISO 868 | 93 | Shore A | |
| Hardness D | ASTM D2240/ISO 868 | 41 | Shore D | |
| Tensile modulus | Injection | ASTMD412 | 39.3 | Mpa |
| Bending modulus | Injection | ASTMD790 | 48.3 | Mpa |
| Taber abraser | ASTMD1044 | 25.0 | mg | |
| Abrasion-DIN | DIN53516 | 25 | mm³ |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| SofteningPoint DMA | 内部方法 | 113 | °C | |
| Glass transition temperature | 内部方法 | -38.0 | °C | |
| Vicat softening temperature | ASTMD1525 | 128 | °C |
| elastomer | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | 100%Strain | ASTMD412 | 10.3 | Mpa |
| 300%Strain | ASTMD412 | 22.8 | Mpa | |
| Tensile strength | ASTMD412 | 44.1 | Mpa | |
| elongation | Break | ASTMD412 | 520 | % |
| Tear strength 2 | ASTMD624 | 133 | kN/m | |
| Permanent compression deformation | 23°C,22hr | ASTMD395B | 25 | % |
| 70°C,22hr | ASTMD395B | 40 | % |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shore hardness | Shore A | ASTMD2240 | 90 |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | DIN 53479 | 1.20 | g/cm³ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.