ASA LI-912 LG CHEM KOREA
287
Unit Price:$2473 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 85MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Weather resistance
- Application Areas:Lighting fixtures
- Color:--
- Grade:Heat resistant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Mold shrinkage rate | Flow | % | ASTM D-955 | 0.40-0.70 |
| Density/specific gravity | g/cm | ASTM D-792 | 1.07 | |
| Kg/m | ISO 1183 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile fracture strain | % | ASTM D-638 | ||
| % | ISO 527-2 | 18 | ||
| Izod notch impact strength | 23℃，3.18mm | J/m | ASTM D-256 | 224 |
| 23℃，6.35mm | J/m | ASTM D-256 | ||
| Tensile modulus | MPa | ISO 527-2 | 2200 | |
| Rockwell hardness | R-Scale | ASTM D-785 | 106 | |
| Bending modulus | MPa | ASTM D-790 | 2250 | |
| bending strength | MPa | ASTM D-790 | 71.7 | |
| Charpy Notched Impact Strength | -30℃ | KJ/m | ISO 179/1eA | 1.70 |
| 23℃ | KJ/m | ISO 179/1eA | 15.8 | |
| Charpy impact strength | -30℃ | KJ/m | ISO 179/1eU | 35.5 |
| 23℃ | KJ/m | ISO 179/1eU | No Break | |
| Tensile yield strength | MPa | ASTM D-638 | 46.9 | |
| MPa | ISO 527-2 | 45.0 | ||
| Tensile yield strain | % | ISO 527-2 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame retardancy | 1.59mm | UL 94 | HB | |
| 3.18mm | UL 94 | HB | ||
| Linear coefficient of thermal expansion | Flow | cm/cm/℃ | ISO 11359-2 | 0.000080 |
| Transverse | cm/cm/℃ | ISO 11359-2 | 0.000080 | |
| Vicat softening temperature | ℃ | ASTM D-1525 | 106 | |
| 50℃/h，B(50N) | ℃ | ISO 306 | 95.9 | |
| Hot deformation temperature | 1.80MPa，Unannealed | ℃ | ASTM D-648 | 92.2 |
| Glass transition temperature | ℃ | ISO 11357-2 | ||
| burning | 3.20mm | ISO 1210 | HB |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Comparative tracking index | IEC 60112 | 600 | ||
| Dielectric strength | kV/mm | IEC 60243-1 | 42 | |
| Relative permittivity | 1MHz | IEC 60250 | 3.20 | |
| Dielectric loss factor | 1MHz | IEC 60250 | 0.033 |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt index | 220℃/10.0kg | g/10min | ASTM D-1238 | |
| 220℃/10kg | cm | ISO 1133 | 10.0 | |
| Water absorption rate | Soultion | % | ISO 62 | 0.36 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.