PEEK KetaSpire® PEEK KT-820CF30 SOLVAY USA
135
- Unit Price:
- $86198 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 17MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Filler: Carbon fiber rein 30% filler by weight
- Application Areas:Solvay Solvie Belgium
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD:3.18mm | ASTMD955 | 0.0到0.20 | % |
| TD:3.18mm | ASTMD955 | 1.5到1.7 | % | |
| Water absorption rate | 24hr | ASTMD570 | 0.10 | % |
| Melt mass flow rate | 400°C/2.16kg | ASTMD1238 | 1.1 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| elongation | Break | ISO527-2/1A/5 | 2.0 | % |
| Bending modulus | -- | ASTMD790 | 17500 | Mpa |
| -- | ISO178 | 20500 | Mpa | |
| bending strength | -- | ASTMD790 | 317 | Mpa |
| -- | ISO178 | 311 | Mpa | |
| compressive strength | ASTMD695 | 173 | Mpa | |
| shear strength | ASTMD732 | 95.1 | Mpa | |
| Poisson's ratio | 7.58 | 0.42 | ||
| Tensile modulus | --4 | ASTMD638 | 19700 | Mpa |
| -- | ISO527-2/1A/1 | 22800 | Mpa | |
| Tensile stress | Yield | ISO527-2/1A/5 | 217 | Mpa |
| -- | ASTMD638 | 201 | Mpa | |
| elongation | Break4 | ASTMD638 | 2.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Annealed | ASTMD648 | 315 | °C |
| Glass transition temperature | ASTMD3418 | 150 | °C | |
| Peak melting temperature | ASTMD3418 | 340 | °C | |
| Linear coefficient of thermal expansion | MD：-50to50°C | ASTME831 | 5.2E-06 | cm/cm/°C |
| specific heat | 50°C | DSC | 1130 | J/kg/°C |
| 200°C | DSC | 1620 | J/kg/°C | |
| thermal conductivity | ASTME1530 | 0.37 | W/m/K |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt viscosity | 400°C,1000sec^-1 | ASTMD3835 | 920 | Pa·s |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Cantilever beam without notch impact strength | -- | ASTMD4812 | 750 | J/m |
| -- | ISO180 | 44 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Scale | ASTMD785 | 105 | |
| Shore hardness | Shore D,1sec | ASTMD2240 | 92 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL94 | V-0 | |
| 1.6mm | UL94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.