PEEK KetaSpire® PEEK KT-820GF30 SOLVAY USA

143

Unit Price:
$86258 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
21MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:high strength Chemical resistance Steam sterilization Fatigue resistance Dimensional stability High temperature resistan High rigidity
Application Areas:film Electronic and Electrical Aircraft Applications Connector Automotive Applications Dental applications
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Water absorption rate	24hr	ASTMD570	0.10	%
Melt mass flow rate	400°C/2.16kg	ASTMD1238	0.70	g/10min
Shrinkage rate 4	MD:3.18mm	ASTMD955	0.20到0.40	%
Shrinkage rate 4	Shrinkage rate 4	TD:3.18mm	ASTMD955	1.4到1.6	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
compressive strength		ASTMD695	169	Mpa
shear strength		ASTMD732	93.1	Mpa
Poisson's ratio		7.58	0.34
Nominal tensile fracture strain	--	ISO527-2/1A/5	2.7	%
Nominal tensile fracture strain	Nominal tensile fracture strain	--6	ASTMD638	2.7	%
Tensile strength	Yield5	ASTMD638	158	Mpa
	Tensile strength	Yield	ISO527-2/1A/5	165	Mpa
	Tensile strength	Tensile strength	--	ASTMD638	158	Mpa
Tensile modulus	--5	ASTMD638	10500	Mpa
Tensile modulus	Tensile modulus	--	ISO527-2/1A/1	11400	Mpa
Bending modulus	--	ISO178	10700	Mpa
Bending modulus	Bending modulus	--	ASTMD790	10300	Mpa
bending strength	--	ASTMD790	271	Mpa
	bending strength	--	ISO178	246	Mpa
	bending strength	bending strength	Yield	ASTMD790	261	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	1.8MPa,Annealed	ASTMD648	315	°C
specific heat	50°C	DSC	1300	J/kg/°C
specific heat	specific heat	200°C	DSC	1730	J/kg/°C
thermal conductivity		ASTME1530	0.29	W/m/K
Glass transition temperature		ASTMD3418	150	°C
Linear coefficient of thermal expansion	MD：-50to50°C	ASTME831	1.7E-05	cm/cm/°C
Peak melting temperature		ASTMD3418	340	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric strength	3.00mm	ASTMD149	17	KV/mm
Surface resistivity		ASTMD257	>1.9E+17	ohms
Dielectric constant	60Hz	ASTMD150	3.44
	Dielectric constant	1kHz	ASTMD150	3.44
	Dielectric constant	Dielectric constant	1MHz	ASTMD150	3.41
Volume resistivity		ASTMD257	1.9E+17	ohms·cm
Dissipation factor	60Hz	ASTMD150	1E-03
	Dissipation factor	1kHz	ASTMD150	1E-03
	Dissipation factor	Dissipation factor	1MHz	ASTMD150	3E-03

Filling analysis	Test Condition	Test Method	Test Result	Unit
Melt viscosity	400°C,1000sec^-1	ASTMD3835	850	Pa·s

Impact performance	Test Condition	Test Method	Test Result	Unit
Cantilever beam without notch impact strength	--	ISO180	56	kJ/m²
Cantilever beam without notch impact strength	Cantilever beam without notch impact strength	--	ASTMD4812	960	J/m

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M-Scale	ASTMD785	100
Shore hardness	Shore D,1sec	ASTMD2240	91

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.6mm	UL94	V-0
UL flame retardant rating	UL flame retardant rating	20.3mm	UL94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.