| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt mass flow rate | 190°C/2.16kg | ASTMD1238 | 2.0 | g/10min |
| Vinyl acetate content | | 内部方法 | 18.0 | wt% |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength | Break | ASTMD638 | 25.5 | Mpa |
| elongation | Break | ASTMD638 | 750 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Brittle temperature | | ASTMD746 | <-70.0 | °C |
| Vicat softening temperature | | ASTMD15252 | 64.0 | °C |
| Melting temperature | | 内部方法 | 86.0 | °C |
| film | Test Condition | Test Method | Test Result | Unit |
|---|
| elongation | MD:Break | ASTMD882 | 200 | % |
| elongation | TD:Break | ASTMD882 | 750 | % |
| Falling hammer impact | | ASTMD1709 | 330 | g |
| Film thickness - tested | | | 50 | µm |
| Tensile strength | MD:Break | ASTMD882 | 23.0 | Mpa |
| Tensile strength | TD:Break | ASTMD882 | 22.6 | Mpa |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore hardness | Shore D | ASTMD2240 | 38 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| gloss | 45° | ASTMD2457 | 75 | |
| Haze | | ASTMD1003 | 2.0 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.