PET Rynite® FR530 NC010 DUPONT USA
267
- Unit Price:
- $4448 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 115MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:enhance Glass fiber reinforced wear resistant High rigidity High temperature resistan
- Application Areas:Electrical field Electronic field Household appliances Household appliances Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1680 | ||
| Molding shrinkage rate | ASTM D955 | 0.8 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate, parallel flow direction | 3.20 mm | ASTM D955 | 0.0025 | cm/cm |
| Shrinkage rate, vertical flow direction | 3.20 mm | ASTM D955 | 0.0075 | cm/cm |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| compressive strength | ASTM D695 | 200 | Mpa | |
| tensile strength | ASTM D638 | 138 | Mpa | |
| Tensile modulus | ASTM D638 | 11000 | Mpa | |
| Bending modulus | ASTM D790 | 10300 | Mpa | |
| bending strength | ASTM D790 | 200 | Mpa | |
| Across Flow | ASTM D638 | 2.1 | % | |
| Low temperature notch impact strength | ASTM D256 | 80 | J/m | |
| Gap impact strength | ASTM D256 | 91 | J/m | |
| bending strength | ASTM D790/ISO 178 | 200 | kg/cm²(MPa)[Lb/in²] | |
| Non notched impact strength | ASTM D256 | 585 | J/m | |
| Tensile modulus | ASTM D412/ISO 527 | 11500 | kg/cm²(MPa)[Lb/in²] | |
| Bending modulus | ASTM D790/ISO 178 | 10500 | kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | 23℃，Injection | MPa | ISO 527-1,-2 | 11500 |
| bending strength | 23℃ | MPa | ISO 178 | |
| Bending modulus | 23℃,压缩模塑 | MPa | ISO 178 | 10500 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.900mm | UL94 | V-0 | |
| 1.50mm | UL94 | V-0 | ||
| 0.750mm | UL94 | V-0 | ||
| Combustibility (rate) | UL94 | V-0 | ||
| Hot deformation temperature | ASTM D648/ISO 75 | 243 | ℃（℉） | |
| ASTM D648/ISO 75 | 225 | ℃（℉） | ||
| melting point | 252 | ℃（℉） | ||
| Hot deformation temperature | 66 psi， Unannealed | ASTM D648 | 246 | °C |
| 264 psi，Unannealed | ASTM D648 | 224 | °C | |
| Linear coefficient of thermal expansion, parallel flow direction | ASTM E831 | 0.000019 | cm/cm/ ℃ | |
| melting point | 254 | °C | ||
| Flame retardant grade | UL 94 | V-0 | ||
| Extreme Oxygen Index | ASTM D2863 | 33 | % | |
| UL flame retardant rating | 0.900mm | UL94 | 5VA | |
| 0.350mm | UL94 | V-0 | ||
| 3.00mm | UL94 | V-0 | ||
| 2.00mm | UL94 | V-0 |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | g/cm³ | ISO 1183 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.