TPE Hytrel® 6356 DUPONT USA
213
- Unit Price:
- $8713 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 11MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability
- Application Areas:Electrical tools Wire and cable Industrial applications pipeline sheet Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density/specific gravity | ISO1183 | 1.22 | g/cm³ | |
| Melt mass flow rate | 230°C/2.16kg | ISO1133 | 9.0 | g/10min |
| Melt volume flow rate | 230°C/2.16kg | ISO1133 | 8.50 | cm3/10min |
| Shrinkage rate | TD | ISO294-4 | 1.5 | % |
| MD | ISO294-4 | 1.5 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.50 | % |
| Saturation,23°C,2.00mm | ISO62 | 0.60 | % | |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.20 | % | |
| MediumDensity | 1.06 | g/cm³ | ||
| SpecificHeatCapacity of Melt | 2150 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.15 | W/m/K |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2 | 280 | Mpa | |
| Tensile stress | Yield | ISO527-2 | 20.0 | Mpa |
| Bending modulus | ISO178 | 290 | Mpa | |
| abrasion resistance | ISO4649 | 110 | mm³ | |
| Tensile stress | Break | ISO527-2 | 43.0 | Mpa |
| 5.0%Strain | ISO527-2 | 12.0 | Mpa | |
| 10%Strain | ISO527-2 | 15.0 | Mpa | |
| 50%Strain | ISO527-2 | 18.8 | Mpa | |
| 100%Strain | ISO527-2 | 19.0 | Mpa | |
| Tensile strain | Yield | ISO527-2 | 31 | % |
| Break | ISO527-2 | >300 | % | |
| Nominal tensile fracture strain | ISO527-2 | 500 | % | |
| TensileCreepModule | 1hr | ISO899-1 | 248 | Mpa |
| Tensile creep modulus | 1000hr | ISO899-1 | 182 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | MD：-- | ISO11359-2 | 1.9E-04 | cm/cm/°C |
| MD：-40to23°C | ISO11359-2 | 1.6E-04 | cm/cm/°C | |
| TD：23to55°C | ASTME831 | 1.7E-04 | cm/cm/°C | |
| TD：-- | ISO11359-2 | 1.8E-04 | cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 1.5E-04 | cm/cm/°C | |
| TD：EffectiveThermalDiffusivity | ISO11359-2 | 5.44E-08 | m²/s | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 80.0 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 45.0 | °C | |
| Brittle temperature | ISO974 | -96.0 | °C | |
| Glass transition temperature 2 | ISO11357-2 | 0.00 | °C | |
| Vicat softening temperature | -- | ISO306/A50 | 195 | °C |
| -- | ISO306/B50 | 100 | °C | |
| Melting temperature 2 | ISO11357-3 | 210 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Relative permittivity | 1MHz | IEC60250 | 4.10 | |
| Dissipation factor | 100Hz | IEC60250 | 0.012 | |
| 1MHz | IEC60250 | 0.036 | ||
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC60093 | 8E+13 | ohms·cm | |
| Dielectric strength | IEC60243-1 | 20 | KV/mm | |
| Relative permittivity | 100Hz | IEC60250 | 4.60 |
| elastomer | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tear strength | Across Flow | ISO34-1 | 150 | kN/m |
| 流量 | ISO34-1 | 160 | kN/m |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -40°C | ISO179/1eA | 15 | kJ/m² |
| -30°C | ISO179/1eA | 25 | kJ/m² | |
| 23°C,Partial Break | ISO179/1eA | 120 | kJ/m² | |
| Impact strength of cantilever beam gap | -40°C | ISO180/1A | 19 | kJ/m² |
| 23°C | ISO180/1A | 81 | kJ/m² | |
| Tensile impact strength | 23°C | ISO8256/1 | 300 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shore hardness | Shore D | ISO868 | 63 | |
| Shore D,15sec | ISO868 | 57 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| 3.0mm | UL94 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| 3.0mm | IEC60695-11-10,-20 | HB | ||
| Extreme Oxygen Index | ISO4589-2 | 21 | % | |
| FMVSS flammability | FMVSS302 | SE | ||
| Fogging-G-value | condensate | ISO6452 | 1E-04 | g |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 2.50 | µgC/g | |
| Odor | VDA270 | 2.50 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.