PA12 UBESTA 3030JI5L UBE JAPAN
198
- Unit Price:
- $14245 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Good flexibility High impact resistance heat-resisting Toughening
- Application Areas:Pipe fittings Automotive sector Pipe fittings
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.01 | kg·cm/cm(J/M)ft·lb/in | |
| Molding shrinkage rate | ASTM D955 | 0.7/1.4 | % | |
| Melt index (flow coefficient) | ASTM D1238/ISO 1133 | 4 | g/10min |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 0.7/1.4 | % | |
| Water absorption rate | ISO 62 | 0.6 | % | |
| Melt index | ISO 1133 | 4 | g/10min | |
| melting point | ISO 11357-3 | 173 | °C | |
| Melt mass flow rate | 235°C/2.16kg | ISO1133 | 4.0 | g/10min |
| Shrinkage rate | TD | ISO294-4 | 1.4 | % |
| MD | ISO294-4 | 0.70 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.60 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Yield | ISO527-2 | 26.0 | Mpa |
| Tensile strain | Yield | ISO527-2 | 24 | % |
| Break | ISO527-2 | 200 | % | |
| Charpy Notched Impact Strength | -，-40℃ | ISO 179/1eA | 4C | KJ/m |
| Bending modulus | ISO178 | 400 | Mpa | |
| Bending stress | ISO178 | 19.0 | Mpa | |
| Tensile yield strength | ISO 527-1/-2 | 26 | Mpa | |
| elongation | Break | ISO 527-1/-2 | ＞200 | % |
| bending strength | ISO 178 | 19 | Mpa | |
| Bending modulus | ISO 178 | 400 | Mpa | |
| Shore hardness | ISO 868 | 67 | D | |
| Rockwell hardness | ISO 2039-2 | 51 | R | |
| Charpy Notched Impact Strength | -，23℃ | ISO 179/1eA | 115P | KJ/m |
| elongation at break | ASTM D412/ISO 527 | ＞200 | % | |
| tensile strength | ASTM D412/ISO 527 | 26 | kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 51 | ||
| Bending modulus | ASTM D412/ISO 527 | 400 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 19 | kg/cm²(MPa)[Lb/in²] |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | ASTM D648/ISO 75 | 91 | ℃（℉） | |
| ASTM D648/ISO 75 | 45 | ℃（℉） | ||
| melting point | 173 | ℃（℉） | ||
| Linear expansion coefficient | ASTM D696/ISO 11359 | 1.7 | mm/mm.℃ | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 91.0 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 45.0 | °C | |
| Melting temperature (DSC) | ISO3146 | 173 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1.7E-04 | cm/cm/°C |
| Hot deformation temperature | -，0.45Mpa | ISO 75-2 | 91 | °C |
| -，1.8Mpa | ISO 75-2 | 45 | °C | |
| Coefficient of linear expansion | ISO 11359-2 | 1.7 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | IEC 60093 | 10 | Ω.cm | |
| IEC60093 | 1E+12 | ohms·cm | ||
| ASTM D257/IEC 60093 | 1012 | Ω.cm |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Sale | ISO2039-2 | 51 | |
| Shore hardness | Shore D | ISO868 | 67 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.