PBT BLUESTAR® 201-G30 202 FNA NANTONG ZHONGLAN

140

Unit Price:
$2087 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
40MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Glass fiber reinforced Processability High rigidity Filler: Glass fiber reinf 30% filler by weight
Application Areas:Electrical field Electronic field Industrial machinery Automotive sector Plastic connectors Electrical/Electronic App Lighting applications
Color:--
Grade:Flame retardant enhanced grade

Technical Data Sheet Compare

Physical properties	Test Condition	Test Method	Test Result	Unit
density		ASTM D792/ISO 1183	1.62
Melt index (flow coefficient)		ASTM D1238/ISO 1133	15-25	g/10min

physical property	Test Condition	Test Method	Test Result	Unit
Melt mass flow rate	250°C/2.16kg	ASTMD1238	16	g/10min
Shrinkage rate	MD	ASTMD955	0.40	%
Shrinkage rate	Shrinkage rate	TD	ASTMD955	0.60	%
Water absorption rate	Equilibrium,23°C,50%RH	ASTMD570	0.16	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus		ASTMD638	10500	Mpa
Tensile strength	Break	ASTMD638	115	Mpa
Bending modulus		ASTMD790	8000	Mpa
bending strength		ASTMD790	180	Mpa
tensile strength		ASTM D638/ISO 527	110	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	8000	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	180	kg/cm²(MPa)[Lb/in²]
IZOD notch impact strength		ASTM D256/ISO 179	7.5	kg·cm/cm(J/M)ft·lb/in

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,Unannealed	ASTMD648	220	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ASTMD648	208	°C
Combustibility (rate)		UL94	V0 3.0mm
Hot deformation temperature		ASTM D648/ISO 75	220	℃（℉）

Electrical performance	Test Method	Test Result	Unit
Volume resistivity	ASTMD257	1.3E+16	ohms·cm
Dielectric strength	ASTMD149	20	KV/mm
Volume resistivity	ASTM D257/IEC 60093	1.3*10e16	Ω.cm

Processing performance	Test Condition	Test Method	Test Result	Unit
Dry conditions			120-140℃ 3-4h
Processing temperature			220-250	°C
	Processing temperature			250-280	°C
	Processing temperature	Processing temperature			240-270	°C
Screw speed			<100	rpm
Mold temperature			60-80	°C
Melt Temperature			250-280	°C
pressure			6-18	Mpa
pressure	pressure			70-120	Mpa

Impact performance	Test Condition	Test Method	Test Result	Unit
Cantilever beam without notch impact strength	23°C	ASTMD256	60.0	kJ/m²

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.8mm	UL94	V-0
UL flame retardant rating	UL flame retardant rating	1.6mm	UL94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.