PBT VALOX™ 357X-1001 SABIC INNOVATIVE US
130
- Unit Price:
- $4617 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant UV resistance
- Application Areas:Electrical appliances Household goods Lighting fixtures
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 250°C/5.0kg | ASTMD1238 | 9.6 | g/10min |
| 265°C/5.0kg | ASTMD1238 | 13 | g/10min | |
| 266°C/5.0kg | ASTMD1238 | 13 | g/10min | |
| Shrinkage rate | MD1 | 内部方法 | 1.1到1.8 | % |
| MD:3.20mm | 内部方法 | 1.0到1.4 | % | |
| TD2 | 内部方法 | 0.90到1.8 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.50 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.15 | % | |
| Melt volume flow rate | 250°C/5.0kg | ISO1133 | 8.00 | cm3/10min |
| 265°C/5.0kg | ISO1133 | 10.0 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Taber abraser | 1000Cycles,1000g,CS-17Wheel | 内部方法 | 33.0 | mg |
| yield | ISO527-2/50 | 50.0 | Mpa | |
| ISO527-2/50 | 5.0 | % | ||
| crack | ISO527-2/50 | 40.0 | Mpa | |
| ISO527-2/50 | 30 | % | ||
| Surrender 4 | ASTMD638 | 50.0 | Mpa | |
| Fracture 5 | ASTMD638 | 40.0 | Mpa | |
| Surrender 6 | ASTMD638 | 5.0 | % | |
| Fracture 7 | ASTMD638 | 30 | % | |
| 50.0mm span 8 | ASTMD790 | 2100 | Mpa | |
| --9 | ISO178 | 2000 | Mpa | |
| --10 | ISO178 | 80.0 | Mpa | |
| Yield, 50.0mm span 11 | ASTMD790 | 78.0 | Mpa | |
| --3 | ASTMD638 | 2000 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 1.8MPa, unannealed, 3.20mm | ASTMD648 | 85.0 | °C | |
| 0.45MPa, unannealed, 3.20mm | ASTMD648 | 130 | °C | |
| -- | ASTMD1525,ISO306/B501322 | 145 | °C | |
| ASTMD1525,ISO306/A501423 | 180 | °C | ||
| ISO306/B120 | 150 | °C | ||
| Flow: -40 to 40 ° C | ASTME831 | 9.2E-05 | cm/cm/°C | |
| Flow: 23 to 80 ° C | ISO11359-2 | 1E-04 | cm/cm/°C | |
| Horizontal: -40 to 40 ° C | ASTME831 | 8.4E-05 | cm/cm/°C | |
| Horizontal: 23 to 80 ° C | ISO11359-2 | 1E-04 | cm/cm/°C | |
| 0.45MPa, unannealed, 100mm span 18 | ISO75-2/Be | 135 | °C | |
| 0.45MPa, unannealed, 64.0mm span 19 | ISO75-2/Bf | 130 | °C | |
| 1.8MPa, unannealed, 100mm span 20 | ISO75-2/Ae | 85.0 | °C | |
| 1.8MPa, unannealed, 64.0mm span 21 | ISO75-2/Af | 85.0 | °C | |
| thermal conductivity | ISO8302 | 0.17 | W/m/K | |
| RTI | UL746 | 140 | °C | |
| BallPressure Test | 125°C | IEC60695-10-2 | Pass | |
| RTIElec | UL746 | 120 | °C | |
| Evolution Calendar intelligent importer | UL746 | 120 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compared to the anti leakage trace index | CTI | UL746 | PLC3 | |
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | ASTMD257,IEC60093 | >1.0E+15 | ohms·cm | |
| Leakage Trace Index | -- | IEC60112 | 225 | V |
| SolutionB | IEC60112 | 100 | V | |
| 1MHz | IEC60250 | 1.3E-03 | ||
| ASTMD150,IEC60250 | 3.00 | |||
| ASTMD150 | 0.013 | |||
| Hot wire ignition | HWI | UL746 | PLC3 | |
| 50Hz | IEC60250 | 3.00 | ||
| IEC60250 | 2E-03 | |||
| 60Hz | IEC60250 | 2E-03 | ||
| IEC60250 | 3.00 | |||
| Arc resistance 24 | ASTMD495 | PLC6 | ||
| 1.60mm,inOil | ASTMD149 | 25 | KV/mm | |
| 3.20mm, inoil | ASTMD149 | 17 | KV/mm | |
| 0.800mm, in oil | IEC60243-1 | 34 | KV/mm | |
| 1.60mm, in oil | IEC60243-1 | 25 | KV/mm | |
| 3.20mm, in oil | IEC60243-1 | 17 | KV/mm | |
| High voltage arc tracing rate | HVTR | UL746 | PLC3 | |
| High arc combustion index | HAI | UL746 | PLC0 |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt viscosity | 260°C,1500sec^-1 | ISO11443 | 310 | Pa·s |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Cantilever beam without notch impact strength | -30°C | ASTMD4812,ISO180/1U | 无断裂 | |
| 23°C | ASTMD4812,ISO180/1U | 无断裂 | ||
| 23°C | ASTMD256 | 500 | J/m | |
| ISO179/2C | 40 | kJ/m² | ||
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 35.0 | J |
| -30°C12 | ISO179/1eA,ISO179/2C | 20 | kJ/m² | |
| 23°C13 | ISO179/1eA | 45 | kJ/m² | |
| Simply supported beam without notch impact strength 14 | -30°C | ISO179/1eU,ISO179/2U | 无断裂 | |
| 23°C | ISO179/1eU,ISO179/2U | 无断裂 | ||
| -30°C | ASTMD256 | 150 | J/m | |
| 0°C | ASTMD256 | 190 | J/m | |
| -30°C15 | ISO180/1A | 10 | kJ/m² | |
| 0°C16 | ISO180/1A | 20 | kJ/m² | |
| 23°C17 | ISO180/1A | 40 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Sale | ISO2039-2 | 115 | |
| Ball pressure hardness | H358/30 | ISO2039-1 | 115 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Extreme Oxygen Index | ISO4589-2 | 30 | % | |
| UL flame retardant rating | 0.750mm | UL94 | V-0 | |
| 2.50mm | UL94 | 5VA | ||
| Burning wire flammability index | 1.00mm | IEC60695-2-12 | 960 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.