PBT Cristin® LW9320 DUPONT USA
110
- Unit Price:
- $3752 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low warpage Filler: Glass fiber reinf 20% by weight ratio) 20% filler by weight Anti warping Good surface performance
- Application Areas:Electronic and electrical Industrial applications Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | -，Across Flow | % | ISO 294-4 | 0.65 |
| -，Flow | % | ISO 294-4 | ||
| Density/specific gravity | g/cm | ISO 1183 | 1.35 | |
| MediumDensity | 1.17 | g/cm³ | ||
| Density/specific gravity | ISO1183 | 1.34 | g/cm³ | |
| Top out temperature | 170 | °C | ||
| SpecificHeatCapacity of Melt | 1900 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.24 | W/m/K | ||
| Melt volume flow rate | 250°C/5.0kg | ISO1133 | 15.0 | cm3/10min |
| Shrinkage rate | TD | ISO294-4 | 0.70 | % |
| MD | ISO294-4 | 0.40 | % | |
| Water absorption rate | Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.30 | % |
| Stickiness number | ISO307 | 120 | cm³/g |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2 | 7500 | Mpa | |
| Tensile stress | Break | ISO527-2 | 120 | Mpa |
| Tensile strain | Break | ISO527-2 | 2.5 | % |
| Bending modulus | ISO178 | 7000 | Mpa | |
| Fracture point tensile stress | 23℃ | MPa | ISO 527-1, -2 | |
| Fracture point tensile strain | % | ISO 527-1, -2 | 2.7 | |
| Tensile modulus | 23℃ | MPa | ISO 527-1, -2 | 7400 |
| Bending modulus | 23℃ | MPa | ISO 178 | 6100 |
| Charpy non notched impact strength | 23 ℃, Type 1, Edgewise | KJ/m | ISO 179 | 55 |
| Charpy notch impact strength | 23 °C, Type 1, Edgewise, Notch A | KJ/m | ISO 179 | 8.5 |
| Gap impact strength | -，-40 ℃, Type 1, Notch A | KJ/m | ISO 180 | |
| -，23 ℃, Type 1, Notch A | KJ/m | ISO 180 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melting temperature | ℃ | ISO 3146 | ||
| Hot deformation temperature | 1.80 Mpa，Unannealed | ℃ | ISO 75A-1, -2 | 180 |
| Flame retardancy | -，0.750 mm | UL94 | HB | |
| -，1.50 mm | UL94 | HB | ||
| -，3.00 mm | UL94 | HB | ||
| Linear coefficient of thermal expansion | TD | ISO11359-2 | 1E-04 | cm/cm/°C |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 175 | °C |
| Glass transition temperature 2 | ISO11357-2 | 110 | °C | |
| Melting temperature 2 | ISO11357-3 | 220 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 3E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Leakage Trace Index | IEC60112 | 500 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 8.5 | kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 45 | kJ/m² |
| 23°C | ISO179/1eU | 50 | kJ/m² | |
| Impact strength of cantilever beam gap | -40°C | ISO180/1A | 7.0 | kJ/m² |
| -30°C | ISO180/1A | 7.0 | kJ/m² | |
| 23°C | ISO180/1A | 7.0 | kJ/m² | |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 8.0 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning rate 3 | 1.00mm | ISO3795 | 30 | mm/min |
| UL flame retardant rating | 0.75mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.75mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| FMVSS flammability | FMVSS302 | B |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 130 | µgC/g | |
| Odor | VDA270 | 3.50 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.