PBT VALOX™ 357U-1001 SABIC INNOVATIVE SHANGHAI
258
Unit Price:$4796 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 231.8MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant UV resistance Impact modification
- Application Areas:Electrical field Electronic field Electrical appliances medicine Medical supplies Nursing supplies Plastic bag Liquid handling Lawn equipment Garden equipment Non specific food Outdoor applications Industrial applications Household goods Architectural application Lighting applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 收缩率 | 流动 : 0.750 到 2.30 mm | 内部方法 | 0.80 到 1.1 | % |
| 流动 : 2.30 到 4.60 mm | 内部方法 | 1.0 到 1.4 | % | |
| 横向流动 : 0.750 到 2.30 mm | 内部方法 | 0.90 到 1.3 | % | |
| 横向流动 : 2.30 到 4.60 mm | 内部方法 | 1.2 到 1.6 | % | |
| 吸水率 | 24 hr | ASTM D570 | 0.080 | % |
| 特定体积 | ASTM D792 | 0.750 | cm³/g | |
| 室外适用性 | UL 746C | f1 |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 伸长率 | 断裂 | ASTM D638 | 110 | % |
| 洛氏硬度 | R 级 | ASTM D785 | 117 | |
| 弯曲模量 | 50.0 mm 跨距 | ASTM D790 | 2060 | Mpa |
| 落锤冲击 | 23°C | ASTM D3029 | 43.0 43.0 | J |
| 无缺口悬臂梁冲击 | 23°C | ASTM D4812 | 3200 | J/m |
| 抗张强度 | 屈服 | ASTM D638 | 48.0 | Mpa |
| 断裂 | ASTM D638 | 48.0 | Mpa | |
| 弯曲强度 | 屈服, 50.0 mm 跨距 | ASTM D790 | 82.0 | Mpa |
| 断裂, 50.0 mm 跨距 | ASTM D790 | 82.0 | Mpa |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 线形热膨胀系数 - 流动 | -40 到 40°C | ASTM E831 | 9.2E-5 | cm/cm/°C |
| 60 到 138°C | ASTM E831 | 1.2E-4 | cm/cm/°C | |
| RTI | UL 746 | 140 | °C | |
| RTI Imp | UL 746 | 120 | °C | |
| RTI Elec | UL 746 | 120 | °C | |
| 载荷下热变形温度 | 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 137 | °C |
| 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 98.0 | °C |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 介电常数 | 100 Hz | ASTM D150 | 3.20 | |
| 1 MHz | ASTM D150 | 3.20 | ||
| 体积电阻率 | ASTM D257 | > 1.2E+16 | ohms·cm | |
| 耗散因数 | 100 Hz | ASTM D150 | 3.0E-3 | |
| 1 MHz | ASTM D150 | 0.030 | ||
| 介电强度 | 1.60 mm, in Oil | ASTM D149 | 25 | KV/mm |
| 3.20 mm, in Air | ASTM D149 | 19 | KV/mm | |
| 3.20 mm, in Oil | ASTM D149 | 19 | KV/mm | |
| 相比耐漏电起痕指数(CTI) | UL 746 | PLC 2 | ||
| 热丝引燃 (HWI) | UL 746 | PLC 2 | ||
| 高电弧燃烧指数(HAI) | UL 746 | PLC 3 | ||
| 高电压电弧起痕速率 (HVTR) | UL 746 | PLC 3 | ||
| 耐电弧性 | ASTM D495 | PLC 6 |
| 注射 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 干燥时间 | 3.0 到 4.0 | hr | ||
| 建议注射量 | 40 到 80 | % | ||
| 料筒后部温度 | 240 到 255 | °C | ||
| 料筒中部温度 | 245 到 260 | °C | ||
| 料筒前部温度 | 250 到 265 | °C | ||
| 射嘴温度 | 245 到 260 | °C | ||
| 背压 | 0.300 到 0.700 | Mpa | ||
| 螺杆转速 | 50 到 100 | rpm | ||
| 排气孔深度 | 0.025 到 0.038 | mm | ||
| 干燥温度 | 120 | °C | ||
| 建议的最大水分含量 | 0.020 | % | ||
| 加工（熔体）温度 | 250 到 265 | °C | ||
| 模具温度 | 50 到 75 | °C |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 极限氧指数 | ASTM D2863 | 30 | % | |
| UL 阻燃等级 | 0.46 mm | UL 94 | HB | |
| 0.64 mm | UL 94 | V-0 | ||
| 3.0 mm | UL 94 | 5VA |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.