PBT Ultradur® S 4090 G6 BASF GERMANY

118

Unit Price:
$4507 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
53MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Enhanced level

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	MD：3.18mm		0.30	%
	Shrinkage rate	TD	ISO294-4	0.75	%
	Shrinkage rate	Shrinkage rate	MD	ISO294-4	0.29	%
Water absorption rate	Saturation	ASTMD570	0.40	%
	Water absorption rate	Saturation,23°C	ISO62	0.40	%
		Water absorption rate	Equilibrium,50%RH	ASTMD570	0.20	%
		Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO62	0.20	%
Viscosity value	降低的粘度	ISO1628	105.0	ml/g
Density/specific gravity		ASTMD792	1.47	g/cm³
Density/specific gravity	Density/specific gravity		ISO1183	1.47	g/cm³
Melt volume flow rate	275°C/2.16kg	ISO1133	20.0	cm3/10min

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile strength	Break,23°C	ASTMD638	125	Mpa
TensileCreepModule	1hr	ISO899-1	7600	Mpa
Tensile creep modulus	1000hr	ISO899-1	6700	Mpa
Tensile modulus	23°C	ISO527-2	9700	Mpa
elongation	Break,23°C	ASTMD638	2.2	%
Bending modulus	23°C	ASTMD790	8270	Mpa
Bending modulus	Bending modulus	23°C	ISO178	8300	Mpa
bending strength	23°C	ASTMD790	194	Mpa
Tensile stress	Break,-40°C	ISO527-2	195	Mpa
	Tensile stress	Break,23°C	ISO527-2	125	Mpa
		Tensile stress	Break,80°C	ISO527-2	79.0	Mpa
			Tensile stress	Break,120°C	ISO527-2	47.0	Mpa
			Tensile stress	Tensile stress	Break,150°C	ISO527-2	35.0	Mpa
Tensile strain	Break,-40°C	ISO527-2	2.4	%
	Tensile strain	Break,23°C	ISO527-2	2.2	%
		Tensile strain	Break,80°C	ISO527-2	3.6	%
			Tensile strain	Break,120°C	ISO527-2	5.9	%
			Tensile strain	Tensile strain	Break,150°C	ISO527-2	4.8	%

Thermal performance	Test Condition	Test Method	Test Result	Unit
RTIElec	0.69mm	UL746	130	°C
	RTIElec	1.5mm	UL746	130	°C
	RTIElec	RTIElec	3.0mm	UL746	130	°C
Evolution Calendar intelligent importer	0.69mm	UL746	90.0	°C
	Evolution Calendar intelligent importer	1.5mm	UL746	90.0	°C
	Evolution Calendar intelligent importer	Evolution Calendar intelligent importer	3.0mm	UL746	90.0	°C
RTIStr	0.69mm	UL746	130	°C
	RTIStr	1.5mm	UL746	130	°C
	RTIStr	RTIStr	3.0mm	UL746	130	°C
Hot deformation temperature	0.45MPa,Unannealed	ASTMD648	210	°C
	Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	210	°C
		Hot deformation temperature	1.8MPa,Unannealed	ASTMD648	177	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	175	°C
Melting temperature (DSC)		ISO3146	223	°C
Linear coefficient of thermal expansion	MD		4E-05	cm/cm/°C
Peak melting temperature		ASTMD3418	223	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Leakage Trace Index		IEC60112	500	V
Surface resistivity 2		ASTMD257	1E+14	ohms
VolumeResistivity	1.50mm	ASTMD257	>1.0E+13	ohms·cm
Surface resistivity		IEC60093	1E+14	ohms
Dielectric constant	100Hz	IEC60250	3.80
Dielectric constant	Dielectric constant	1MHz	IEC60250	3.70
Volume resistivity		IEC60093	>1.0E+13	ohms·cm
Dissipation factor	100Hz	IEC60250	3E-03
Dissipation factor	Dissipation factor	1MHz	IEC60250	0.018

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO179	50	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179	59	kJ/m²
Charpy Notched Impact Strength	23°C	ISO179	9.0	kJ/m²
Impact strength of cantilever beam gap	-40°C	ASTMD256	69	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTMD256	85	J/m

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.69mm	UL94	HB
	UL flame retardant rating	1.5mm	UL94	HB
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.