PBT Crastin® SK605 DUPONT TAIWAN
130
- Unit Price:
- $3268 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 65MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Filler: Glass fiber reinf 30% by weight ratio) 30% filler by weight Good strength Good hardness (glass fibe 30% by weight ratio) 30% filler by weight Good strength Good hardness (glass fibe
- Application Areas:Electronic and electrical Industrial applications household electrical appl Structural components switch Automotive Applications Shell Spool
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density/specific gravity | ASTM D792 | 1.53 | ||
| ISO1183 | 1.53 | g/cm³ | ||
| Melt mass flow rate | ISO1133 | 10 | g/10min | |
| MediumDensity | 1.36 | g/cm³ | ||
| Top out temperature | 170 | °C | ||
| Melt volume flow rate | 250°C/2.16kg | ISO1133 | 7.00 | cm3/10min |
| Shrinkage rate | TD | ISO294-4 | 1.1 | % |
| MD | ISO294-4 | 0.30 | % | |
| Water absorption rate | Saturation,23°C,2.00mm | ISO62 | 0.35 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.15 | % | |
| Stickiness number | ISO307 | 100 | cm³/g | |
| SpecificHeatCapacity of Melt | 1730 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.28 | W/m/K |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2 | 10000 | Mpa | |
| Tensile stress | Break | ISO527-2 | 140 | Mpa |
| Tensile strain | Break | ISO527-2 | 2.7 | % |
| TensileCreepModule | 1hr | ISO899-1 | 9000 | Mpa |
| Tensile creep modulus | 1000hr | ISO899-1 | 6600 | Mpa |
| Bending modulus | ISO178 | 9000 | Mpa | |
| Bending stress | ISO178 | 200 | Mpa | |
| compressive strength | 5 mm/min, 3.20 mm, 23 ℃ | MPa | ASTM D695 | 202 |
| tensile strength | 23℃ | MPa | ASTM D638 | 140 |
| Tensile modulus | 23℃ | MPa | ASTM D638 | 10000 |
| Bending modulus | 23℃ | MPa | ASTM D790 | 8970 |
| bending strength | 23℃ | MPa | ASTM D790 | |
| Across Flow | 23℃ | % | ASTM D638 | 2.6 |
| Low temperature notch impact strength | J/m | ASTM D256 | 101 | |
| Gap impact strength | -，-40℃ | J/m | ASTM D256 | 101 |
| -，23℃ | J/m | ASTM D256 | 112 | |
| Non notched impact strength | -，-40℃ | J/m | ASTM D256 | 1120 |
| -，23℃ | J/m | ASTM D256 | 998 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | -，0.45Mpa,Unannealed | ℃ | ASTM D648 | |
| -，1.8Mpa,Unannealed | ℃ | ASTM D648 | 205 | |
| Linear coefficient of thermal expansion | 平行Flow ，73 to 130°F (23 to 55℃) | cm/cm/℃ | ASTM E831 | 0.000030 |
| 垂直Flow ，73 to 130°F (23 to 55℃) | cm/cm/℃ | ASTM E831 | 0.000090 | |
| melting point | ℃ | 225 | ||
| Flame retardant grade | -，0.750 mm | UL 94 | HB | |
| -，1.50 mm | UL 94 | HB | ||
| -，3.00 mm | UL 94 | HB | ||
| Linear coefficient of thermal expansion | TD | ISO11359-2 | 9E-05 | cm/cm/°C |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 220 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 205 | °C | |
| Vicat softening temperature | ISO306/B50 | 215 | °C | |
| Melting temperature 2 | ISO11357-3 | 224 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 3E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Dielectric strength | IEC60243-1 | 38 | KV/mm | |
| Relative permittivity | 100Hz | IEC60250 | 3.90 | |
| 1MHz | IEC60250 | 3.80 | ||
| Dissipation factor | 100Hz | IEC60250 | 7.5E-04 | |
| 1MHz | IEC60250 | 0.018 | ||
| Leakage Trace Index | IEC60112 | 400 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -40°C | ISO179/1eA | 10 | kJ/m² |
| -30°C | ISO179/1eA | 11 | kJ/m² | |
| 23°C | ISO179/1eA | 10 | kJ/m² | |
| Impact strength of simply supported beam without notch | -40°C | ISO179/1eU | 75 | kJ/m² |
| -30°C | ISO179/1eU | 75 | kJ/m² | |
| 23°C | ISO179/1eU | 70 | kJ/m² | |
| Impact strength of cantilever beam gap | -40°C | ISO180/1A | 10 | kJ/m² |
| -30°C | ISO180/1A | 10 | kJ/m² | |
| 23°C | ISO180/1A | 11 | kJ/m² | |
| Unscented Izod impact strength | -40°C | ISO180/1U | 55 | kJ/m² |
| -30°C | ISO180/1U | 55 | kJ/m² | |
| 23°C | ISO180/1U | 60 | kJ/m² |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Extreme Oxygen Index | % | ASTM D2863 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning rate 3 | 1.00mm | ISO3795 | 41 | mm/min |
| UL flame retardant rating | 0.75mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.75mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| Extreme Oxygen Index | ISO4589-2 | 19 | % | |
| FMVSS flammability | FMVSS302 | B | ||
| Fogging-F-value | refraction | ISO6452 | 99 | % |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 140 | µgC/g | |
| Odor | VDA270 | 3.00 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.