PPO NORYL™ FE1520PW-73701 SABIC INNOVATIVE NETHERLANDS
152
- Unit Price:
- $6128 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 16.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Hot water resistance Low water absorption
- Application Areas:valve shower head Water pump impeller Faucet
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt volume flow rate | 280°C/10.0kg | ISO1133 | 22.0 | cm3/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.20to0.40 | % |
| TD：3.20mm | 内部方法 | 0.30to0.60 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.20 | % |
| Equilibrium,50%RH | ASTMD570 | 0.060 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus 2 | ASTMD638 | 7110 | Mpa | |
| Tensile modulus | ISO527-2/1 | 7180 | Mpa | |
| Tensile strength 3 | Break | ASTMD638 | 119 | Mpa |
| Tensile stress | Break | ISO527-2/5 | 119 | Mpa |
| Elongation rate 4 | Break | ASTMD638 | 2.6 | % |
| Tensile strain | Break | ISO527-2/5 | 2.6 | % |
| Bending modulus 4 | 50.0mmSpan | ASTMD790 | 6970 | Mpa |
| Bending modulus 5 | ISO178 | 6040 | Mpa | |
| Bending strength 5,6 | ISO178 | 165 | Mpa | |
| Bending strength 5 | Break,50.0mmSpan | ASTMD790 | 175 | Mpa |
| Taber abraser | 1000Cycles,1000g,CS-17Wheel | 内部方法 | 65.0 | mg |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature 9 | 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 139 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 135 | °C |
| Hot deformation temperature 9 | 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 132 | °C |
| Vicat softening temperature | -- | ISO306/A50 | 150 | °C |
| -- | ISO306/B120 | 144 | °C | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ISO11359-2 | 3E-05 | cm/cm/°C |
| TD：-40to40°C | ISO11359-2 | 7E-05 | cm/cm/°C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| CharpyUnnotchImpactStrength7 | 23°C | ISO179/1eU | 30 | kJ/m² |
| Suspended wall beam gap impact strength 8 | -30°C | ISO180/1A | 4.0 | kJ/m² |
| 23°C | ISO180/1A | 6.0 | kJ/m² | |
| Unscented Izod Impact Strength 8 | -30°C | ISO180/1U | 23 | kJ/m² |
| 23°C | ISO180/1U | 25 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | H358/30 | ISO2039-1 | 220 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.