PPO XYRON™ 540Z ASAHI JAPAN
274
- Unit Price:
- $3534 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 63MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant High temperature resistan
- Application Areas:Electrical field Electronic field Industrial machinery Automotive sector Automotive interior parts
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.45 | ||
| Molding shrinkage rate | ASTM D955 | 0.4-1.1 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | ASTM D-955 | 0.5-0.7 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| bending strength | 23℃,50%RH | ASTM D-790 | 1000 | kg/cm |
| Bending modulus | 23℃,50%RH | ASTM D-790 | 25000 | kg/cm |
| tensile strength | 23℃,50%RH | ASTM D-638 | 700 | kg/cm |
| Izod impact strength | 6.4mm带切口23℃ | ASTM D-256 | 15 | Kg cm/cm |
| Fracture elongation rate | 23℃,50%RH | ASTM D-638 | 50 | % |
| elongation at break | ASTM D638/ISO 527 | 3.3 | % | |
| Tensile modulus | ASTM D638/ISO 527 | 7482 | kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 117 | kg/cm²(MPa)[Lb/in²] | |
| Bending modulus | ASTM D790/ISO 178 | 6137 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 179 | kg/cm²(MPa)[Lb/in²] | |
| IZOD notch impact strength | ASTM D256/ISO 179 | 69 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 18.6Kg/cm | ASTM D-648 | 120 | °C |
| Flame resistance | 1.6mm | UL-94 | V-0 | |
| Hot deformation temperature | ASTM D648/ISO 75 | 220 | ℃（℉） | |
| ASTM D648/ISO 75 | 203 | ℃（℉） | ||
| melting point | 225 | ℃（℉） |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric tangent | 23℃,50%RH,10 | ASTM D-150 | 0.0027 | |
| Dielectric constant | 23℃,50%RH,10 | ASTM D-150 | 2.7 | |
| Arc resistance | 钨电极 | ASTM D-495 | 70 | Secretary |
| Surface resistivity | 23℃,50%RH | ASTM D-257 | 10 | Ω |
| dielectric breakdown strength | 短时间法2mm厚 | ASTM D-149 | 26 | KV/mm |
| Volume resistivity | 23℃,50%RH | ASTM D-257 | 10 | Ω.cm |
| Surface resistivity | ASTM D257/IEC 60093 | 0.016E15 | Ω | |
| Dielectric constant | ASTM D150/IEC 60250 | 3.8 | ||
| ASTM D150/IEC 60250 | 3.6 | |||
| Volume resistivity | ASTM D257/IEC 60093 | 2.3e15 | Ω.cm |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | 23℃,50%RH,24Hr | ASTM D-570 | 0.10 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.