PPO NORYL™ N190X-71283 SABIC INNOVATIVE SHANGHAI

119

Unit Price:
$3506 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:transparent High temperature resistan
Application Areas:Automotive components Illuminating lamp
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Water absorption rate	24 hr	ASTM D570	0.080	%
Outdoor applicability		UL 746C	f1
Melt flow rate	280°C/5.0 kg	ASTM D1238	20	g/10 min
Molten Volume Flow Rate (MVR)	280°C/5.0 kg	ISO 1133	23.0	cm3/10min
Shrinkage rate - flow	3.20 mm	内部方法	0.50 到 0.70	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Bending stress	-- 6, 7	ISO 178	87.0	Mpa
	Bending stress	Yield, 50.0 mm Span 4	ASTM D790	98.0	Mpa
	Bending stress	Bending stress	Yield, 100 mm Span 5	ASTM D790	91.0	Mpa
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	ASTM D1044	76.0	mg
Tensile strength	Yield 3	ASTM D638	60.0	Mpa
	Tensile strength	Yield	ISO 527-2/50	58.0	Mpa
		Tensile strength	Break 3	ASTM D638	47.0	Mpa
		Tensile strength	Tensile strength	Break	ISO 527-2/50	50.0	Mpa
Tensile modulus	-- 2	ASTM D638	2580	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2600	Mpa
elongation	Yield 3	ASTM D638	3.6	%
	elongation	Yield	ISO 527-2/50	3.2	%
		elongation	Break 3	ASTM D638	9.0	%
		elongation	elongation	Break	ISO 527-2/50	9.2	%
Bending modulus	50.0 mm Span 4	ASTM D790	2500	Mpa
	Bending modulus	100 mm Span 5	ASTM D790	2300	Mpa
	Bending modulus	Bending modulus	-- 6	ISO 178	2350	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Vicat softening temperature	--	ASTM D15259	104	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	107	°C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.7E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	8.1E-5	cm/cm/°C
thermal conductivity		ASTM C177	0.24	W/m/K
RTI		UL 746	95.0	°C
RTI Imp		UL 746	80.0	°C
RTI Elec		UL 746	95.0	°C
Thermal deformation temperature under load	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	95.0	°C
	Thermal deformation temperature under load	0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span 8	ISO 75-2/Bf	95.0	°C
		Thermal deformation temperature under load	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	78.0	°C
			Thermal deformation temperature under load	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	86.0	°C
			Thermal deformation temperature under load	Thermal deformation temperature under load	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 8	ISO 75-2/Af	82.0	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric strength	3.20 mm, in Oil	ASTM D149	19	KV/mm
Compared to the Leakage Tracking Index (CTI)		UL 746	PLC 1
Hot wire ignition (HWI)		UL 746	PLC 2
High Voltage Arc Traceability Rate (HVTR)		UL 746	PLC 4
High arc combustion index (HAI) 11		UL 746	PLC 2
Arc resistance 10		ASTM D495	PLC 7
Dissipation factor	100 Hz	ASTM D150	0.013
Dissipation factor	Dissipation factor	100 kHz	ASTM D150	5.5E-3
Dielectric constant	100 Hz	ASTM D150	2.74
Dielectric constant	Dielectric constant	100 kHz	ASTM D150	2.60
Volume resistivity		ASTM D257	1.8E+16	ohms·cm

injection	Test Result	Unit
drying temperature	75 到 80	°C
Suggested maximum moisture content	0.020	%
Processing (melt) temperature	250 到 275	°C
Mold temperature	55 到 75	°C
drying time	3.0 到 4.0	hr
Suggested injection volume	30 到 70	%
Temperature at the rear of the barrel	215 到 265	°C
Temperature in the middle of the barrel	225 到 270	°C
Temperature at the front of the material cylinder	240 到 275	°C
Spray nozzle temperature	250 到 275	°C
Back pressure	0.300 到 0.700	Mpa
Screw speed	20 到 100	rpm
Exhaust hole depth	0.038 到 0.051	mm

Impact performance	Test Condition	Test Method	Test Result	Unit
Dart impact equipped with measuring instruments	23°C, Total Energy	ASTM D3763	50.0	J
Non notched cantilever beam impact	23°C	ASTM D4812	720	J/m

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	R-Scale	ASTM D785	120

flammability	Test Condition	Test Method	Test Result	Unit
Extreme Oxygen Index		ASTM D2863	39	%
UL flame retardant rating	1.0 mm	UL 94	HB
	UL flame retardant rating	1.5 mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	5VA

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.