PPO NORYL™ PX9406-701 SABIC INNOVATIVE US
253
Unit Price:$3490 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 25.2MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant
- Application Areas:Household appliances Household appliances Automotive interior parts Electronic communication Electronic communication
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Flow : 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
| Across Flow 2 | 内部方法 | 0.50 到 0.70 | % | |
| Water absorption rate | 24 hr | ASTM D570 | 0.060 | % |
| Outdoor applicability | UL 746C | f2 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Elongation rate | Yield | ASTM D638 | 9.5 | % |
| Break | ASTM D638 | 18 | % | |
| Non notched cantilever beam impact | 23°C | ASTM D4812 | 1100 | J/m |
| Tensile strength | Yield | ASTM D638 | 75.0 | Mpa |
| Break | ASTM D638 | 55.0 | Mpa | |
| Dart impact equipped with measuring instruments | 23°C, Energy at Peak | ASTM D3763 | 42.0 | J |
| Bending modulus | 100 mm Span | ASTM D790 | 2640 | Mpa |
| bending strength | Yield, 100 mm Span | ASTM D790 | 111 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Thermal deformation temperature under load | 0.45 MPa, Unannealed, 6.40 mm | ASTM D648 | 133 | °C |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 122 | °C | |
| Vicat softening temperature | ASTM D15255 | 150 | °C | |
| RTI | UL 746 | 110 | °C | |
| RTI Imp | UL 746 | 105 | °C | |
| RTI Elec | UL 746 | 110 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 2 | ||
| High arc combustion index (HAI) | UL 746 | PLC 0 | ||
| Hot wire ignition (HWI) | UL 746 | PLC 0 | ||
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 4 | ||
| Arc resistance | ASTM D495 | PLC 6 | ||
| Surface resistivity | ASTM D257 | > 1.0E+16 | ohms | |
| Dielectric constant | 60 Hz | ASTM D150 | 2.57 | |
| 50 kHz | ASTM D150 | 2.57 | ||
| 1 MHz | ASTM D150 | 2.49 | ||
| Volume resistivity | ASTM D257 | 2.0E+16 | ohms·cm | |
| Dissipation factor | 50 Hz | ASTM D150 | 5.2E-3 | |
| 60 Hz | ASTM D150 | 5.2E-3 | ||
| 1 MHz | ASTM D150 | 2.6E-3 | ||
| Dielectric strength | 3.20 mm, in Oil | ASTM D149 | 19 | KV/mm |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying time | 3.0 到 4.0 | hr | ||
| Suggested injection volume | 30 到 70 | % | ||
| Temperature at the rear of the barrel | 245 到 295 | °C | ||
| Temperature in the middle of the barrel | 255 到 300 | °C | ||
| Temperature at the front of the material cylinder | 265 到 305 | °C | ||
| Spray nozzle temperature | 275 到 305 | °C | ||
| Back pressure | 0.300 到 0.700 | Mpa | ||
| Screw speed | 20 到 100 | rpm | ||
| Exhaust hole depth | 0.038 到 0.051 | mm | ||
| drying temperature | 105 到 110 | °C | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Processing (melt) temperature | 275 到 305 | °C | ||
| Mold temperature | 70 到 100 | °C |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.76 mm | UL 94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.