PC Makrolon® FR6005 901510 COVESTRO SHANGHAI
140
- Unit Price:
- $2877 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 172.6MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Easy to demould Impact resistance Aging resistance
- Application Areas:Electronic and electrical
- Color:--
- Grade:--
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Mass-Flow Rate | 300°C 1.2kg | ISO 1133 | 9 | cm3/10min |
| Density | ISO 1183 | 1200 | kg/m3 | |
| Modeling Shrinkage (Flow) | ISO 2577 | 0.6~0.8 | % | |
| Modeling Shrinkage (Across Flow) | ISO 2577 | 0.6~0.8 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Modulus | 0mm/min | ISO 527 | 2300 | Mpa |
| Tensile Strength (Yield 50mm/min) | ISO 527 | 62 | Mpa | |
| Tensile Strength (Break 50mm/min) | ISO 527 | 66 | Mpa | |
| Tensile Elongation (Yield, 50mm/min) | ISO 527 | 6 | % | |
| Tensile Elongation (Break, 50mm/min) | ISO 527 | 50 | % | |
| ISO 527 | 135 | % | ||
| Flexural Strength (2.0mm/min) | ISO 178 | 90 | Mpa | |
| Flexural Modulus (2.0mm/min) | ISO 178 | 2400 | Mpa | |
| Notched Izod Impact Strength (23℃ 3.0mm ) | ISO 180 | 60 | kJ/m² | |
| Notched Izod Impact Strength (-10℃ 3.0mm ) | ISO 180 | 50 | kJ/m² | |
| Notched Izod Impact Strength (-30℃ ) | ISO 180 | 15 | kJ/m² | |
| Charpy Notched Impact Strength (23°C) | ISO 179 | 68 | kJ/m² | |
| Charpy Notched Impact Strength (-10°C) | ISO 179 | 50 | kJ/m² | |
| Charpy Notched Impact Strength (-30°C) | ISO 179 | 20 | kJ/m² | |
| Film Puncture Force | ISO 6603 | 5100 | N | |
| Film Puncture Force | ISO 6603 | 6100 | N | |
| Film Puncture Force | ISO 6603 | 54 | J | |
| Film Puncture Force | ISO 6603 | 55 | J |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8Mpa) | ISO 75 | 121 | °C | |
| Deflection Temperature Under Load (0.45Mpa) | ISO 75 | 136 | °C | |
| Vicat Softening Temperature | ISO 306 | 142 | °C | |
| Vicat Softening Temperature | ISO 306 | 144 | °C | |
| Coefficient of Linear Thermal Expansion (Flow 23~55°C) | ISO 11359 | 0.000070 | cm/cm/°C | |
| Coefficient of Linear Thermal Expansion (Across Flow 23~55°C) | ISO 11359 | 0.000070 | cm/cm/°C | |
| Ball Indentation Hardness | ISO 11359-2 | 134 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume Resistivity | IEC 60093 | 90000000000000000 | Ω.m | |
| Comparative Tracking Index | IEC 60112 | 200 | V | |
| Surface Resistivity | IEC 60093 | 400000000000000000 | Ω |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.