PC Makrolon® ET3113 550115 COVESTRO SHANGHAI

123

Unit Price:
$2143 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
235.8MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Weather resistance Hydrolysis resistance
Application Areas:PC board Electrical field Electronic field Other sheets Automotive sector
Color:--
Grade:Extrusion grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Across Flow	ISO 2577	0.60 到 0.80	%
	Modeling Shrinkage	流量	ISO 2577	0.60 到 0.80	%
		Modeling Shrinkage	Across Flow : 280°C, 2.00 mm 4	ISO 294-4	0.75	%
		Modeling Shrinkage	Modeling Shrinkage	流量 : 2.00 mm 4	ISO 294-4	0.70	%
Moisture Absorption	Saturation, 23°C	ISO 62	0.30	%
Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.12	%
Melt Mass-Flow Rate	300°C/1.2 kg	ISO 1133	6.5	g/10 min
Melt Volume flow Rate	300°C/1.2 kg	ISO 1133	6.00	cm3/10min
Apparent Density		ISO 60	0.66	g/cm³
Density	23°C	ISO 1183	1.20	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Strain at Flexural Strength	23°C	ISO 178	7.2	%
Flexural Stress	23°C	ISO 178	96.0	Mpa
Flexural Stress	Flexural Stress	3.5% Strain, 23°C	ISO 178	72.0	Mpa
Nominal Tensile Strain at Break	23°C	ISO 527-2/50	> 50	%
Tensile Stress	Yield, 23°C	ISO 527-2/50	65.0	Mpa
Tensile Stress	Tensile Stress	Break, 23°C	ISO 527-2/50	70.0	Mpa
Tensile Strain	Yield, 23°C	ISO 527-2/50	6.3	%
Tensile Strain	Tensile Strain	Break, 23°C	ISO 527-2/50	130	%
Tensile Creep Modulus	1 hr	ISO 899-1	2200	Mpa
Tensile Creep Modulus	Tensile Creep Modulus	1000 hr	ISO 899-1	1900	Mpa
Tensile Modulus	23°C	ISO 527-2/1	2350	Mpa
Flexural Modulus	23°C	ISO 178	2350	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45 MPa, Unannealed	ISO 75-2/B	141	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed	ISO 75-2/A	128	°C
RTI	1.5 mm	UL 746	125	°C
RTI Imp	1.5 mm	UL 746	115	°C
RTI Elec	1.5 mm	UL 746	125	°C
Thermal Conductivity	23°C	ISO 8302	0.20	W/m/K
Vicat Softening Temperature	--	ISO 306/B50	148	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/B120	149	°C
Linear thermal expansion coefficient	Flow : 23 to 55°C	ISO 11359-2	6.5E-5	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : 23 to 55°C	ISO 11359-2	6.5E-5	cm/cm/°C
Glass Transition Temperature		ISO 11357-2	148	°C
Ball PressureTest	140°C	IEC 60695-10-2	通过

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength	23°C, 1.00 mm	IEC 60243-1	34	KV/mm
Relative Permittivity	23°C, 100 Hz	IEC 60250	3.10
Relative Permittivity	Relative Permittivity	23°C, 1 MHz	IEC 60250	3.00
Comparative Tracking Index	Solution A	IEC 60112	250	V
Comparative Tracking Index	Comparative Tracking Index	Solution B	IEC 60112	125	V
Dissipation Factor?	23°C, 100 Hz	IEC 60250	8.0E-4
Dissipation Factor?	Dissipation Factor?	23°C, 1 MHz	IEC 60250	0.010
Surface Resistivity		IEC 60093	1.0E+16	ohms
Volume Resistivity	23°C	IEC 60093	1.0E+16	ohms·cm

Film	Test Condition	Test Method	Test Result	Unit
Water Vapor Transmission Rate	23°C, 85% RH, 100 µm	ISO 15106-1	15	g/m²/24 hr
Carbon Dioxide Permeability	23°C, 25.4 µm	ISO 2556	16900	cm³/m²/bar/24 hr
Gas Permeation	Carbon Dioxide : 100.0 µm	ISO 2556	3800	cm³/m²/bar/24 hr
	Gas Permeation	Nitrogen : 25.4 µm	ISO 2556	510	cm³/m²/bar/24 hr
		Gas Permeation	Nitrogen : 100.0 µm	ISO 2556	120	cm³/m²/bar/24 hr
			Gas Permeation	Oxygen : 25.4 µm	ISO 2556	2760	cm³/m²/bar/24 hr
			Gas Permeation	Gas Permeation	Oxygen : 100.0 µm	ISO 2556	650	cm³/m²/bar/24 hr

Impact Properties	Test Condition	Test Method	Test Result	Unit
Notched Izod Impact Strength	-30°C, Complete Break	ISO 180/A	20	kJ/m²
Notched Izod Impact Strength	Notched Izod Impact Strength	23°C, Partial Break	ISO 180/A	70	kJ/m²
Charpy Notched Impact Strength	-30°C, Complete Break	ISO 179/1eA	18	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C, Partial Break	ISO 179/1eA	80	kJ/m²
Multi-Axial Instrumented Impact Energy	-30°C	ISO 6603-2	70.0	J
Multi-Axial Instrumented Impact Energy	Multi-Axial Instrumented Impact Energy	23°C	ISO 6603-2	60.0	J
Multi-Axial Instrumented Impact Peak Force	-30°C	ISO 6603-2	6500	N
Multi-Axial Instrumented Impact Peak Force	Multi-Axial Instrumented Impact Peak Force	23°C	ISO 6603-2	5600	N
Charpy Unnotched Impact Strength	-60°C	ISO 179/1eU	无断裂
	Charpy Unnotched Impact Strength	-30°C	ISO 179/1eU	无断裂
	Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO 179/1eU	无断裂

hardness	Test Condition	Test Method	Test Result	Unit
Ball Indentation Hardness		ISO 2039-1	113	Mpa

optical performance	Test Condition	Test Method	Test Result	Unit
Index of Refraction		ISO 489	1.587
Electrolytical Corrosion	23°C	IEC 60426	A1
ISO Shortname			ISO 7391-PC,EL,(,,)-09-9
Transmittance	1000 µm	ISO 13468-2	89.0	%
	Transmittance	2000 µm	ISO 13468-2	89.0	%
		Transmittance	3000 µm	ISO 13468-2	88.0	%
		Transmittance	Transmittance	4000 µm	ISO 13468-2	87.0	%
Haze	3000 µm	ISO 14782	< 0.80	%

Flammability	Test Condition	Test Method	Test Result	Unit
Oxygen Index		ISO 4589-2	28	%
Flash Ignition Temperature		ASTM D1929	480	°C
Needle Flame Test	1.50 mm 12	IEC 60695-11-5	1.0	min
	Needle Flame Test	2.00 mm 12	IEC 60695-11-5	2.0	min
		Needle Flame Test	2.00 mm 13	IEC 60695-11-5	0.1	min
			Needle Flame Test	3.00 mm 12	IEC 60695-11-5	2.0	min
			Needle Flame Test	Needle Flame Test	3.00 mm 13	IEC 60695-11-5	0.2	min
Self Ignition Temperature		ASTM D1929	550	°C
Glow Wire Flammability Index	0.75 mm	IEC 60695-2-12	875	°C
	Glow Wire Flammability Index	1.5 mm	IEC 60695-2-12	875	°C
	Glow Wire Flammability Index	Glow Wire Flammability Index	3.0 mm	IEC 60695-2-12	960	°C
Glow Wire Ignition Temperature	0.75 mm	IEC 60695-2-13	875	°C
	Glow Wire Ignition Temperature	1.5 mm	IEC 60695-2-13	875	°C
	Glow Wire Ignition Temperature	Glow Wire Ignition Temperature	3.0 mm	IEC 60695-2-13	900	°C
Burning Rate	> 1.00 mm	ISO 3795	passed
Flame Rating	1.5 mm	UL 94	HB
Flame Rating	Flame Rating	0.75 mm	UL 94	V-2
Application of Flame from Small Burner 11		DIN 53438-1, -3	K1, F1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.